A high-performance magnetorheological material: Preparation, characterization and magnetic-mechanic coupling properties

Yangguang Xu,Xinglong Gong,Shouhu Xuan,Wei Zhang,Yanceng Fan

DOI: https://doi.org/10.1039/c1sm05301a

IF: 4.046

2011-01-01

Soft Matter

Abstract:A novel high-performance magnetorheological material, named as magnetorheological plastomer (MRP), was developed by dispersing iron particles into a plastic polyurethane (PU) matrix. The dynamic properties (including storage modulus and loss factor) of the MRP material were systematically tested and the influences of the iron particle content and magnetic field were analyzed. It is found that the anisotropic MRP product with 80% iron particle weight fraction (A-MRP-80), shows a high dynamic property: the maximum magneto-induced storage modulus is 6.54 MPa; the relative MR effect reaches as high as 532%; the loss factor can be reduced to 0.03 by adjusting magnetic field. This kind of MRP shows a much higher magnetorheological performance than the previously reported magnetorhelogical elastomer (MRE). The mechanism for its high MR performance was proposed and the influence of the iron particle distribution and temperature on the dynamic properties were discussed.