High frequency needle ultrasonic transducers based on Mn doped piezoelectric single crystal
Xiao Yang,Zhaoxi Li,Chunlong Fei,Yangbin Liu,Di Li,Shang Hou,Lin Zhang,Fei Li,Yintang Yang,Qifa Zhou,Zhuo Xu
DOI: https://doi.org/10.1016/j.jallcom.2020.154951
IF: 6.2
2020-08-01
Journal of Alloys and Compounds
Abstract:<p>This paper describes the design, fabrication and imaging application of high frequency needle-type transducers based on manganese doped Pb(In<sub>1/2</sub>Nb<sub>1/2</sub>)O<sub>3</sub>-Pb(Mg<sub>1/3</sub>Nb<sub>2/3</sub>)-PbTiO<sub>3</sub>(Mn: PIN-PMN-PT) piezoelectric single crystals. The grown Mn: PIN-PMN-PT single crystals have a piezoelectric coefficient <em>d</em><sub><em>33</em></sub> of 1200 pc/N, an electromechanical coupling factor <em>k</em><sub><em>t</em></sub> of 54%, and Curie temperature of 220 °C. Mn: PIN-PMN-PT single crystals based transducers with one and two matching layers show center frequency of 48 MHz, 47.1 MHz and −6 dB bandwidth of 36.7%, 41.8% respectively. Zebrafish have been imaged by these transducers, which shows the potential applications of these Mn: PIN-PMN-PT single crystals based transducers in high resolution biological imaging. Electrical impedance and phase of Mn: PIN-PMN-PT transducers were measured at temperature from 40 °C to 160 °C and the trend of changes was explained by the Mason model in different situations. It was found that the Mn: PIN-PMN-PT can maintain good performance at temperatures as high as 140 °C. The result shows that the Mn: PIN-PMN-PT has superior piezoelectric properties comparable to PIN-PMN-PT and its thermal stability is higher than PMN-PT.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering