Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Anodic Formation of Anatase TiO2 Nanotubes with Rod-Formed Walls for Photocatalysis and Field Emitters

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Tube-In-Tube Tio2 Nanotubes with Porous Walls: Fabrication, Formation Mechanism, and Photocatalytic Properties

Titania Nanowires Synthesized by Thermal Oxidation of Ti Plates in Vacuum

Titania Nanoflowers with High Photocatalytic Activity

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Univariate Lattice Parameter Modulation of Single-Crystal-like Anatase TiO2 Hierarchical Nanowire Arrays to Improve Photoactivity

Hierarchical Wall Formation of Titanium Oxide Nanotube Arrays Using Anodic Oxidation

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Array of Single Crystalline Anatase TiO2 Nanotubes with Significant Enhancement of Photoresponse

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Synthesis of immobilized TiO2 nanowires by anodic oxidation and their gas phase photocatalytic properties

Fabrication and Photocatalysis of TiO2 Flower-like Nanostructures

Biocompatible and freestanding anatase TiO2 nanomembrane with enhanced photocatalytic performance.

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays

Direct Synthesis of Anatase Tio2 Nanowires with Enhanced Photocatalytic Activity