Abstract:Void distribution maps and corresponding mean Feret diameter. Void defect is prevalent during the composite manufacturing process and may reduce the mechanical properties of composite structures, while limited information about three‐dimensional void distribution and evolution can be found due to the difficulties in void observation. In this work, void defects at different positions were detected and analyzed using x‐ray microtomography (XRM), and the random forest algorithm was implemented for segmenting components of CFRP samples. Results showed a trend of gradual rising porosity in the axial direction, with an increase of ~250% of porosity at the outlet of resin injection compared to the one at the inlet during the composite manufacturing process. The voids mainly featured with microscale between carbon fibers, with less distribution between fiber bundles and resin‐rich zones. Void defects achieved aggregation at the middle position of manufactured laminate, which is probably related to pressure interception. In the axial direction, the proportion of large‐diameter voids gradually increased, and a large volume of connected voids appeared near the outlet. Due to the shear deformation of resin and fiber and the pressure gradient effect, most of the voids showed stripe shape. The spatial orientation of voids was predominantly along the direction of resin flow and fluctuated due to fiber curl. Highlights 3D void characteristics in CFRP were studied using the XRM technique. Void formation and the effects of fibers on void morphology were analyzed. Dynamic void transport mechanisms during CFRP manufacturing were studied. Location and morphology of voids are helpful for CFRP damage modeling. The effective partitioning of CFRP was achieved using a random forest algorithm.

Investigations on Void Morphology in CFRP Composite Materials and Ultrasonic Scattering Attenuation Based on a 2D Random Void Model

Numerical Investigations of Ultrasonic Scattering from Voids in Composite Materials Based on Random Void Model

Researches on the Ultrasonic Scattering Attenuation of Carbon Fibre Reinforced Plastics with 2D Real Morphology Void Model

Ultrasonic attenuation model of void contained carbon-fiber reinforced plastics

A Novel 2-D Random Void Model and Its Application in Ultrasonically Determined Void Content for Composite Materials

A novel random void model and its application in predicting void content of composites based on ultrasonic attenuation coefficient

Cfrp Voids 3d Identification and Location Method Based on the Process of Backscattered Signal

Machine Learning and Materials Informatics Approaches for Predicting Transverse Mechanical Properties of Unidirectional CFRP Composites with Microvoids

Frequency Spectral Analysis for the Ultrasonic Attenuation of Carbon Fiber Reinforced Plastics

Ultrasonic Inspection Of Localized Defects In Low-Porosity Cfrp

Geometric Simulation of 2-D Morphology of Voids in Composites Based on the Random Medium Model

Modeling of Digital Spectrum Based Ultrasonic Attenuation about Void Content in CFRP

Ultrasonic attenuation testing method for NDE of void content based on theoretical model and experiment calibration

Porosity Test in Carbon Composites Based on a New Ultrasonic Attenuation Method

Random Void Modeling for Carbon Fibre Reinforced Composite with Highly Dispersed Void Size

Micro‐mesoscopic analysis of 3D void formation and evolution in CFRP composite using high‐resolution x‐ray microtomography

Comparison Between 2-D Deterministic Model and Random Model of Voids in Composite Materials

Identification of Localized Void Defects in Composite by Recurrence Quantification Analysis of Ultrasonic Backscattered Signal

Modeling of Ultrasonic Testing about Void Content in Carbon Fibre

Influence of irregular-void on transverse tensile mechanical properties of composites

The Influence of Void Distribution on Transverse Mechanical Properties of Unidirectional Composites