Abstract:Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly attractive for high-field applications, especially in particle accelerator magnets, nuclear magnetic resonance spectrometers, medical magnetic resonance imaging systems and nuclear fusion reactors. Herein, through an industrially scalable and cost-effective manufacturing strategy, a practical level critical current density up to 1.1x10^5 A/cm2 at 4.2 K in an external magnetic field of 10 T was achieved in Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 superconducting tapes. The preparation strategy combines flat rolling to induce grain texture and a subsequent hot-isostatic-pressing densification. By varying the parameters of rolling, the degree of grain texture was engineered. It is found that the transport properties of the Ba1-xKxFe2As2 tapes can be enhanced by applying a large amount of deformation during rolling, which can be attributed to the improved degree of c-axis texture. Microstructure characterizations on the highest-performance tape demonstrate that the Ba1-xKxFe2As2 phase has a uniform element distribution and small grains with good connectivity. Grain boundary pinning is consequently enhanced as proved by large currents circulating through the sample even at 25 K. Our work proves that Cu/Ag composite sheathed Ba1-xKxFe2As2 superconducting tapes can be a promising competitor for practical high-field applications in terms of the viable, scalable and cost-effective fabrication strategy applied and the high transport properties achieved in this work.

High critical current density and low anisotropy in textured Sr 1−x K x Fe 2 As 2 tapes for high field applications

High critical current density and low anisotropy in textured Sr₁-xKxFe₂As₂ tapes for high field applications.

High Transport Critical Current Densities in Textured Fe-sheathed Sr1−xKxFe2As2+Sn Superconducting Tapes

Textured Sr1-xKxFe2As 2 superconducting tapes with high critical current density

Realization of Practical Level Current Densities in Sr0.6K0.4Fe2As2 Tape Conductors for High-Field Applications

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

Strongly Enhanced Current Densities in Sr0.6K0.4Fe2As2 + Sn Superconducting Tapes

Superior Transport Current Densities in (ba, K)Fe2As2 Superconducting Tapes Realized by Combined Strengthening of Grain Texture and Flux Pinning

Large transport critical currents and magneto-optical imaging of textured Sr1-xKxFe2As2 superconducting tapes

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

High Critical Current Density in Textured Ba-122/Ag Tapes Fabricated by A Scalable Rolling Process

Hot Pressing to Enhance the Transport Jc of Sr0.6K0.4Fe2As2 Superconducting Tapes.

Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors

High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

Large Transportjcin Sn-added SmFeAsO1−xFxtapes Prepared by Anex Situpit Method

Transport Critical Current Density of High-Strength Sr1−xKxFe2As2/Ag/Monel Composite Conductors

Development of high-performance iron-based superconducting wires and tapes

Critical Current and Flux Pinning Characteristics in Sr0.6K0.4Fe2As2 Superconducting Tapes

Microstructure and transport critical current in Sr0.6K 0.4Fe2As2 superconducting tapes prepared by cold pressing