Abstract:Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly attractive for high-field applications, especially in particle accelerator magnets, nuclear magnetic resonance spectrometers, medical magnetic resonance imaging systems and nuclear fusion reactors. Herein, through an industrially scalable and cost-effective manufacturing strategy, a practical level critical current density up to 1.1x10^5 A/cm2 at 4.2 K in an external magnetic field of 10 T was achieved in Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 superconducting tapes. The preparation strategy combines flat rolling to induce grain texture and a subsequent hot-isostatic-pressing densification. By varying the parameters of rolling, the degree of grain texture was engineered. It is found that the transport properties of the Ba1-xKxFe2As2 tapes can be enhanced by applying a large amount of deformation during rolling, which can be attributed to the improved degree of c-axis texture. Microstructure characterizations on the highest-performance tape demonstrate that the Ba1-xKxFe2As2 phase has a uniform element distribution and small grains with good connectivity. Grain boundary pinning is consequently enhanced as proved by large currents circulating through the sample even at 25 K. Our work proves that Cu/Ag composite sheathed Ba1-xKxFe2As2 superconducting tapes can be a promising competitor for practical high-field applications in terms of the viable, scalable and cost-effective fabrication strategy applied and the high transport properties achieved in this work.

Hot Pressing to Enhance the Transport Jc of Sr0.6K0.4Fe2As2 Superconducting Tapes.

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

Textured Sr1-xKxFe2As 2 superconducting tapes with high critical current density

Development of high-performance iron-based superconducting wires and tapes

High Transport Critical Current Densities in Textured Fe-sheathed Sr1−xKxFe2As2+Sn Superconducting Tapes

Tailoring the Critical Current Properties in Cu-sheathed Sr1−xKxFe2As2superconducting Tapes

Observation of reversible critical current performance under large compressive strain in Sr0.6K0.4Fe2As2 tapes

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils

High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

Critical Current and Flux Pinning Characteristics in Sr0.6K0.4Fe2As2 Superconducting Tapes

Superconductivity of Powder-In-Tube Sr0.6k0.4fe2as2 Wires

Transport Critical Currents in the Iron Pnictide Superconducting Wires Prepared by the Ex Situ Pit Method

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

Iron-Based Superconductors for High-Field Applications: Realization of High Engineering Critical Current Density

Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors

High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication

Electromechanical properties of iron and silver sheathed Sr0.6K0.4Fe2As2 tapes

Progress in wire fabrication of iron-based superconductors

Transport Current Density At Temperatures Up To 25k Of Cu/Ag Composite Sheathed 122-Type Tapes And Wires

Superconducting joint between iron-based superconductor tapes