Abstract:The Bi 2 Sr 2 CaCu 2 O x (Bi-2212) precursor powder has been successfully synthesized using the spray pyrolysis method, and the powder has also been made into high critical current density Bi-2212/Ag-alloy wire with 666 filaments through the oxide-powder-in-tube (PIT) and the partial-melt processing (PMP). The advantage of low segregation was found in the spray pyrolysis precursor powder due to the gas-film-barrier high-temperature calcination for the micro-sized atomized solution droplets during the spray pyrolysis process. The droplets are instantly transformed into nearly nano-sized spherical oxide powder, and the liquid phase segregation could only appear inside each of these powder spheres during the process. And the elemental content and elemental distribution in each droplet are perfectly uniform, improving the homogeneity of the final oxide powder. In conventional precursor powders that have only undergone a solid phase sintering, the liquid phase flows between the powders, resulting in severe segregation. As the segregation phenomenon was almost avoided, the content of the Bi 2 Sr 2 CuO x (Bi-2201) phase and (Sr, Ca) x Cu y O z (alkaline earth cuprates, AEC) phase in the precursor powder decreased, leading to the enhancement of the Bi-2212 content in the precursor powder and the conductive characteristics of the wire. The superconducting critical transition temperature T c of the final wire is 90.53 K, and the Δ T c value is only 0.08 K. The wire has a small Δ T c value, further indicating the higher purity of the superconducting sample. The critical current density ( J c ) of the Bi-2212 wire reaches 283 A/mm 2 at 65 K in self-field, which is higher than that of the wire reported in the literature. After high-pressure heat treatment, the highest J e and the highest J c of the wires reach 538 A/mm 2 and 2987 A/mm 2 at 4.2 K & 12T. It indicated that the spray pyrolysis method would be a candidate method for preparing high-performance Bi-2212 wire.

Superconductivity of Powder-In-Tube Sr0.6k0.4fe2as2 Wires

Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method

Superconducting Properties of Granular Smfeaso1-Xfx Wires with T-C=52 K Prepared by the Powder-In-Tube Method

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

Superconductivity of powder-in-tube LaO0.9F0.1FeAs wires

Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes

Development of high-performance iron-based superconducting wires and tapes

Low-temperature synthesis of SmFeAsO0.7F0.3 wires with high transport critical current density

Superconducting properties and magneto-optical imaging of Ba0.6K0.4Fe2As2 PIT wires with Ag addition

Role of heat and mechanical treatments in the fabrication of superconducting Ba0.6K0.4Fe2As2 ex-situ Powder-In-Tube tapes

Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors

Enhancement of Critical Current Densities in (Ba,K)Fe2As2 by 320 MeV Au Irradiation in Single Crystals and by High-Pressure Sintering in PIT Wires

Fabrication and Superconducting Properties of MgB2 Wires with Amorphous Carbon Doping by In-situ Powder-in-tube Method

Superconducting properties of the powder-in-tube Cu-Mg-B and Ag-Mg-B wires

High critical current density in low-cost iron-based superconducting round wires annealed at ambient pressure

Preparation of high-performance high temperature superconducting Bi-2212 wires by the spray pyrolysis powder

Iron-Based Superconductors for High-Field Applications: Realization of High Engineering Critical Current Density

Transport properties of iron-based FeTe0.5Se0.5 superconducting wire