Abstract:The recent discovery of superconductivity in the iron based superconductors with very high upper critical fields presents a new possibility for practical applications, but fabricating fine-wire is a challenge because of mechanically hard and brittle powders and the toxicity and volatility of arsenic. In this paper, we report the synthesis and the physical characterization of iron pnictide wires and bulks prepared by the powder-in-tube method (PIT). A new class of high-Tc iron pnictide composite wires, such as LaFeAsO1-xFx, SmFeAsO1-xFx and Sr1-xKxFeAs, has been fabricated by the in situ PIT technique using Fe, Ta and Nb tubes. Microscopy and x-ray analysis show that the superconducting core is continuous, and retains phase composition after wire drawing and heat treatment. Furthermore, the wires exhibit a very weak Jc-field dependence behavior even at high temperatures. The upper critical field Hc2(0) value can exceed 100 T, surpassing those of MgB2 and all the low temperature superconductors and indicating a strong potential for applications requiring very high field. These results demonstrate the feasibility of producing superconducting pnictide composite wire. We also applied the one step PIT method to synthesize the iron-based bulks, due to its convenience and safety. In fact, by using this technique, we have successfully discovered superconductivity at 35 K and 15 K in Eu0.7Na0.3Fe2As2 and SmCoFeAsO compounds, respectively. These clearly suggest that the one-step PIT technique is unique and versatile and hence can be tailored easily for other rare earth derivatives of novel iron-based superconductors.

Transport properties of iron-based FeTe0.5Se0.5 superconducting wire

Transport Critical Currents in the Iron Pnictide Superconducting Wires Prepared by the Ex Situ Pit Method

Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method

Progress in wire fabrication of iron-based superconductors

Critical Current Density and AC Magnetic Susceptibility of High-Quality FeTe0.5Se0.5 Superconducting Tapes

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

Low-temperature synthesis of SmFeAsO0.7F0.3 wires with high transport critical current density

Superconducting properties of FeSe wires and tapes prepared by a gas diffusion technique

Superconducting properties of FeSe wires and tapes prepared by gas diffusion technique

Exploring the feasibility of Fe(Se,Te) conductors by ex-situ Powder-in-Tube method

Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils

High critical current density in low-cost iron-based superconducting round wires annealed at ambient pressure

High Transport Current Superconductivity in Powder-in-tube Ba0.6K0.4Fe2As2 Tapes at 27T

Superconducting Properties of Granular Smfeaso1-Xfx Wires with T-C=52 K Prepared by the Powder-In-Tube Method

Bulk Superconductivity in Fe1+yTe0.6Se0.4 Induced by Removal of Excess Fe

Robust superconductivity and transport properties in (Li1-xFex)OHFeSe single crystals

Superconductivity of Powder-In-Tube Sr0.6k0.4fe2as2 Wires

Anisotropic Superconducting Properties of FeSe0.5Te0.5 Single Crystals

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

Low-Temperature Synthesis of Smfeaso0.7f0.3-Delta Wires with A High Transport Critical Current Density

Critical current density and microstructure of iron sheathed multifilamentary Sr1-xKxFe2As2/Ag composite conductors