Abstract:Uniform anatase TiO2 nanocuboids enclosed by active {100} and {001} facets over a wide size range (60-830 nm in length) with controllable aspect ratios were solvothermally synthesized through hydrolysis of titanium tetraisopropoxide (TTIP) using acetic acid (HAc) as the solvent and the ionic liquid 1-butyl-3-methylimidazolium tetrafluoroborate ([bmim][BF4]) as the capping agent. The size and aspect ratio of the anatase TiO2 nanocuboids can be readily adjusted by changing the composition parameters including the contents of [bmim][BF4], water, and HAc in the quaternary solution system. It was revealed that [bmim][BF4] played an important role in stabilizing both the {100} and {001} facets of the anatase TiO2 nanocuboids. On the one hand, [bmim][BF4] acted as a fluoride source to release F-ions for stabilizing the {001} facets; on the other hand, the [bmim](+) ions acted as effective capping ions to preferentially stabilize the {100} facets. The obtained near-monodisperse anatase TiO2 nanocuboids exhibited an interesting self-assembly behavior during deposition. These single-crystalline anatase nanocuboids showed extremely high crystalline phase stability, retaining the pure phase of anatase as well as the morphology even after being calcined at 900 degrees C. Moreover, the anatase nanocuboids exhibited considerably enhanced photocatalytic activity owing the wholly exposed active {100} and {001} facets.

Low Temperature Solvothermal Synthesis Of Anatase Tio2 Single Crystals With Wholly {100} And {001} Faceted Surfaces

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Anatase TiO2 single crystals with a large percentage of reactive facets

One-pot synthesis of N-F-Cr-doped anatase TiO₂ microspheres with nearly all-(001) surface for enhanced solar absorption.

Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets

Low-Temperature Synthesis of High-Ordered Anatase Tio2 Nanotube Array Films Coated with Exposed {001} Nanofacets

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Hydrothermal Growth of Nanometer- to Micrometer-Size Anatase Single Crystals with Exposed (001) Facets and Their Ability to Assist Photodegradation of Rhodamine B in Water.

Synthesis of Anatase Tio2 Nanocrystals with Exposed {001} Facets

Facile synthesis of anatase TiO2 mesocrystal sheets with dominant {001} facets based on topochemical conversion

Hydrothermal growth of multi-facet anatase spheres

Shape‐ and Size‐Controlled Synthesis of Uniform Anatase TiO2 Nanocuboids Enclosed by Active {100} and {001} Facets

Fast synthesis of anatase TiO2 single crystals by a facile solid-state method

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Controllable synthesis of anatase TiO 2 with nano-carved surface morphologies

Anatase TiO2 film with dominant (001) facets prepared by radio frequency atmospheric pressure plasma

Formation and Evolution of the High-Surface-Energy Facets of Anatase Tio2

Facet-dependent Decoration of TiO2 Mesocrystals on TiO2 Microcrystals for Enhanced Photoactivity

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature