Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets
Luoyuan Ruan,Xinwei Wang,Tongyao Wang,Zhaohui Ren,Ying Chen,Ruoyu Zhao,Dikui Zhou,Gangjie Fu,Shi Li,Lina Gao,Yunhao Lu,Zhiyu Wang,He Tian,Xueqian Kong,Gaorong Han
DOI: https://doi.org/10.1021/acsami.9b11233
IF: 9.5
2019-01-01
ACS Applied Materials & Interfaces
Abstract:Facet engineering of anatase TiO2 by controlling the {001} exposure ratio has been the focus of numerous investigations to optimize photocatalytic activity. In particular, an introduction of fluoride ions during the crystal growth has been demonstrated to be very effective and decisive in realizing the facet exposure of the crystals. However, a key role of fluoride ions in stabilizing {001} exposure and improving subsequent photocatalytic activity of anatase TiO2 remains unclear up to date. Herein, a controlled thickness of anatase TiO2 nanosheets has been realized by introducing different amounts of ethanol into a HF acid-assisted hydrothermal reaction. The thinnest nanosheets with a thickness of similar to 2.9 nm were evaluated to have the highest H-2 production rate of 41.04 mmol.h(-1).g(-1) under ultraviolet light irradiation, and the corresponding quantum efficiency was determined to be 41.6% (lambda = 365 nm). Moreover, it is proved for the first time that fluoride ions are bonded with Ti vacancies on {001} facets, and such defects are crucial for stabilizing the ultrathin nanosheets and improving their electron-hole separation, therefore leading to a highly efficient photocatalytic activity. The findings offer an opportunity to engineer facets and functionality of anatase TiO2 by controlling surface defects.