Disclosing the true atomic structure of {001} facets in shape-engineered TiO2 anatase nanoparticles

Stefano Pantaleone,Francesco Pellegrino,Valter Maurino,Marta Corno,Piero Ugliengo,Lorenzo Mino
DOI: https://doi.org/10.1039/d3ta06694k
IF: 11.9
2024-01-24
Journal of Materials Chemistry A
Abstract:In the last decade shape-engineering of TiO 2 anatase nanoparticles (NPs) has attracted increasing attention owing to the possibility to maximize the presence of {001} facets, which have been reported to show peculiar adsorption, electronic, and (photo)catalytic properties. It is well-known that the anatase (001) surface is prone to reconstruction and several models have been proposed and validated by DFT calculations and single crystal studies. However, its true atomic structure in shape-engineered TiO 2 anatase nanoparticles often remains elusive. In this study we shed light on this issue combining IR spectroscopy of CO adsorbed at very low temperature and thorough DFT modelling. Our results show that the thermal treatment in oxygen, performed to remove the capping agents ( i.e. , fluorides) employed in the synthesis of shape-controlled NPs, leads to a reconstruction of the {001} facets which is compatible with an "add-oxygen" model (AOM) and not with the most commonly reported "add-molecule" model (ADM). These findings can guide future experimental and computational studies highlighting that the AOM reconstruction is the most appropriate model to describe the properties and reactivity of the {001} facets in shape-controlled TiO 2 nanoparticles after thermal removal of fluorides.
materials science, multidisciplinary,chemistry, physical,energy & fuels
What problem does this paper attempt to address?
This paper aims to solve the problem of the real atomic structure of the {001} crystal plane in titanium anhydride (TiO₂) nanoparticles in shape engineering. Specifically, the research focuses on the reconstruction of the {001} crystal plane after removing the capping agent (such as fluoride) used to control the shape at high temperatures. By combining infrared spectroscopy (IR spectroscopy) and density functional theory (DFT) modeling, the authors explored whether the atomic structure of the {001} crystal plane conforms to the "Add - Oxygen Model" (AOM) or the "Add - Molecule Model" (ADM). ### Main problems 1. **Real atomic structure of the {001} crystal plane**: The research attempts to reveal the actual atomic structure of the {001} crystal plane in TiO₂ nanoparticles in shape engineering after removing the capping agent. 2. **Selection of reconstruction models**: Determine whether the {001} crystal plane is more in line with the AOM model or the ADM model after high - temperature treatment. ### Research methods - **Experimental part**: - **Synthesis**: TiO₂ nano - sheets with exposed {001} crystal planes and TiO₂ bipyramids with mainly exposed {101} crystal planes were synthesized by the solvothermal method. - **Characterization**: The samples were characterized by X - ray diffraction (XRD), high - resolution transmission electron microscopy (HR - TEM), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FT - IR). - **Heat treatment**: The samples were heat - treated in air at 873 K to remove the capping agent. - **Computational part**: - **DFT calculation**: Periodic DFT calculations were carried out using the Vienna Ab initio Simulation Package (VASP) to optimize the geometric structure and calculate the frequency. - **Surface model**: Models of the (101), (100) and (001) surfaces were constructed, and two reconstruction models (ADM and AOM) of the (001) surface were considered. - **Adsorption energy and vibration frequency**: The adsorption energy and vibration frequency of CO molecules on different surfaces were calculated and compared with the experimental results. ### Main findings - **Experimental results**: Through FT - IR spectroscopy, it was found that at the maximum CO coverage, the main peak of the bipy sample was at 2178 cm⁻¹, while the main peak of the n - sh sample was at 2155 cm⁻¹, and as the CO coverage decreased, the peak shifted to 2159 cm⁻¹. - **Calculation results**: DFT simulations showed that the CO adsorption frequency of the AOM model was closer to the experimental results, and its adsorption energy was lower, which explained the phenomenon of easier CO desorption from the {001} crystal plane observed in the experiment. ### Conclusions - **The AOM model is more appropriate**: The research results support the AOM model as the most appropriate model for describing the {001} crystal plane structure after removing the capping agent under high - temperature oxidation conditions. - **Guiding significance**: These findings provide guidance for future experimental and computational research, emphasizing the superiority of the AOM model in describing the properties and reactivity of the {001} crystal plane.