Performance of Pvdf-Hfp-Based Gel Polymer Electrolytes with Different Pore Forming Agents

Wei Xiao,Xinhai Li,Zhixing Wang,Huajun Guo,Yan Li,Bo Yang

DOI: https://doi.org/10.1007/s13726-012-0081-7

IF: 2.485

2012-01-01

Iranian Polymer Journal

Abstract:Poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP)-based gel polymer electrolytes (GPEs) with polyvinylpyrrolidone (PVP) and urea as a pore forming agent, respectively, were fabricated by phase inversion method. Physicochemical properties of the as-prepared polymer electrolytes were characterized by SEM, XRD, TG, electrochemical impedance spectroscopy (EIS) and linear sweep voltammetry (LSV). The results showed that the GPE membranes using urea as pore forming agent present a uniform surface with abundant interconnected micro-pores and possess upto 330 °C decomposition temperature; the XRD patterns indicate that adding urea into the polymer matrix can attain more amorphous areas than adding PVP; the reciprocal temperature dependence of ionic conductivity of as-prepared GPEs follows Vogel-Tamman-Fulcher relation and the ionic conductivity at room temperature is 2.212 mS cm−1 for PVP pore forming GPEs and 2.823 mS cm−1 for urea pore forming GPEs, respectively; the interfacial resistance of the Li/GPEs/Li cell using urea as pore forming agent can achieve a quick steady value of about 660 Ω cm−1 lower than that of PVP of about 760 Ω cm−1 during the same storage conditions; the electrochemical stability window of the GPEs with urea can be stable upto 5.0 V (vs. Li+/Li) at room temperature. The battery performance of the assembled Li/GPEs/LiCoO2 coin cell also showed that the cell using urea as pore forming agent in GPEs demonstrated excellent first charge/discharge rate and cycle performances. These excellent physicochemical and battery properties indicated that urea can be used as a kind of excellent pore forming agent for polymer electrolytes in the lithium-ion polymer battery.