Abstract:In this paper, the competing requirements of material strength, casting formation and residual stress are considered in the design of a large bulkhead integral isothermal forging die using a design approach that incorporates an outer ring plus a die body. Thermal stress assembly was conducted to resolve the various manufacturing issues encountered in the production of this large-scale casting. This paper also proposes a design method for an expansion joint and material-saving holes to homogenize the cross-sectional thickness of the casting die by solving problems associated with defects and hot cracking during the casting process. The finite element method was used based on the equivalent liquid level descending method, the Niyama criterion, etc., to analyze the pouring of the sand model with different risers to choose the casting process. To resolve the occurrence of hot cracks during production, the design was optimized and the process was improved in combining with the simulation analysis result, after which carrying out another finite element analysis and by re-verifying the production process again. The results show that the simulated porosity, shrinkage and stress distribution are in accord with the practical production status. Based on the mechanical properties and a microstructure analysis, the tension strength of the K3 casting die at 950 °C is approximately 635 MPa, and the microstructures are typical dendrites. However, through the simulation, practical production, and analysis of the mechanical properties and microstructure, the die design method proposed in this paper offers benefits in solving casting forming problems and hot cracking of an integral oversized titanium bulkhead casting die, and a K3 superalloy die with a weight of 7.8 tons was successfully cast.

Failure Analysis of Nozzle Body for Zinc-alloy Die Casting and Measures of Improving its Service Life

The Analysis of Influing Factor of the Failure of Nozzle Body in Zinc-alloy Die Casting

Failure Analysis of M300 Steel for Nozzle Body in Zinc Alloy Die Casting Machine

Research on the Corrosion Behavior of Low Carbon Mold Flux on Submerged Nozzle Refractory

Research on the Improvement of Soundness AG 40 A Zinc Alloy Casting

Impacts of Zinc Layer and Pouring Method on Interface Performance for Al-22Si/ZL104 Bi-Metal

Improved Strength and Enhanced Pitting Corrosion Resistance of Al-Mn Alloy with Zr Addition

Investigation on Surface Defects Produced in Pretreatment of Die-casting AM60B Magnesium Alloy

Fracture Analysis of Die-casting Mould for Water Pump

Investigation and Improvement Strategies for Mold Fracture: A Study on the Application of a Pulse Electrodeposition Method for Enhancing Mold Lifespan

Quantitative study of the effect of high-performance zinc alloy coating technology on the life of mechanical components

Analysis and Measures of Blockage in Submerged Nozzle of Mold large round Bearing Steel

Eliminating Defects of ZnAl Alloy by Squeeze Casting or Liquid Extrusion

Study of properties of Ni-base nano-ZrO2 composite plating coatings

Investigation on RE Ion Nitro-carbnrizing Treatment Used for 3Cr2W8V Die Casting Mold

The development of low-temperature heat-treatable high-pressure die-cast Al–Mg–Fe–Mn alloys with Zn

Performance Enhancements of High-Pressure Die-Casting Die Processed by Biomimetic Laser-Remelting Process

Casting Design Optimization Using Numerical Simulation of Precision Forging Die for Large Titanium Alloy Integral Bulkhead

Relationship of Compositions, Phase Constituents and Solidification Paths of Casting Mg-Al-Zn Alloys

Thermal stress analysis and structural optimization of ladle nozzle based on finite element simulation