Abstract:Fast-growth of single crystal monolayer graphene by CVD using methane and hydrogen has been achieved on "homemade" single crystal Cu/Ni(111) alloy foils over large area. Full coverage was achieved in 5 min or less for a particular range of composition (1.3 at.% to 8.6 at.% Ni), as compared to 60 min for a pure Cu(111) foil under identical growth conditions. These are the bulk atomic percentages of Ni, as a superstructure at the surface of these foils with stoichiometry Cu6Ni1 (for 1.3 to 7.8 bulk at.% Ni in the Cu/Ni(111) foil) was discovered by low energy electron diffraction (LEED). Complete large area monolayer graphene films are either single crystal or close to single crystal, and include folded regions that are essentially parallel and that were likely wrinkles that "fell over" to bind to the surface; these folds are separated by large, wrinkle-free regions. The folds occur due to the buildup of interfacial compressive stress (and its release) during cooling of the foils from 1075 °C to room temperature. The fold heights measured by atomic force microscopy (AFM) and scanning tunneling microscopy (STM) prove them to all be 3 layers thick, and scanning electron microscopy (SEM) imaging shows them to be around 10 to 300 nm wide and separated by roughly 20 μm. These folds are always essentially perpendicular to the steps in this Cu/Ni(111) substrate. Joining of well-aligned graphene islands (in growths that were terminated prior to full film coverage) was investigated with high magnification SEM and aberration-corrected high-resolution transmission electron microscopy (TEM) as well as AFM, STM, and optical microscopy. These methods show that many of the "join regions" have folds, and these arise from interfacial adhesion mechanics (they are due to the buildup of compressive stress during cool-down, but these folds are different than for the continuous graphene films-they occur due to "weak links" in terms of the interface mechanics). Such Cu/Ni(111) alloy foils are promising substrates for the large-scale synthesis of single-crystal graphene film.

Layer-controlled and wafer-scale synthesis of uniform and high-quality graphene films on a polycrystalline nickel catalyst

A Novel Preparation Method for Uniform Large-Area Graphene Films on Ni@Cu Substrate

Characterization Of Graphene Grown On Bulk And Thin Film Nickel

Controlled Growth of Large-Area Monolayer Graphene on Ni (110) Facet: Insight from Molecular Dynamics Simulation

Direct growth of single-layer graphene on Ni surface manipulated by Si barrier

One-step Chemical Vapor Synthesis of Ni/graphene Nanocomposites with Excellent Electromagnetic and Electrocatalytic Properties

Preparation of few-layer graphene by annealing Ni film with low carbon content deposited by direct current magnetron sputtering

Synthesis of Single-Layer Graphene on Nickel Using A Droplet Cvd Process

Heteroepitaxial Growth Of Wafer Scale Highly Oriented Graphene Using Inductively Coupled Plasma Chemical Vapor Deposition

Synthesis and characterization of large-area graphene and graphite films on commercial Cu-Ni alloy foils.

Segregation Growth of Graphene on Cu–Ni Alloy for Precise Layer Control

Single-layer Graphene Nearly 100% Covering an Entire Substrate

Synthesis of Large Area, Homogeneous, Single Layer Graphene Films by Annealing Amorphous Carbon on Co and Ni

Controllable Chemical Vapor Deposition of Large Area Uniform Nanocrystalline Graphene Directly on Silicon Dioxide

Direct chemical vapor deposition growth of graphene on Ni particles using solid carbon sources

Graphene synthesis by chemical vapor deposition and transfer by a roll-to-roll process

Highly Oriented Monolayer Graphene Grown on a Cu/Ni(111) Alloy Foil.

Continuous Epitaxy of Single-Crystal Graphite Films by Isothermal Carbon Diffusion Through Nickel.

Review of Chemical Vapor Deposition of Graphene and Related Applications

Uniform Single-Layer Graphene Growth on Recyclable Tungsten Foils

Synthesis of graphene on a Ni film by radio-frequency plasma-enhanced chemical vapor deposition