Structure and Piezoelectric Properties of Bifeo3 and Bi0.92dy0.08feo3 Multiferroics at High Temperature

Chen Sun,Xiaomin Chen,Junling Wang,Guoliang Yuan,Jiang Yin,Zhiguo Liu

DOI: https://doi.org/10.1016/j.ssc.2012.04.067

IF: 1.934

2012-01-01

Solid State Communications

Abstract:Multiferroic BiFeO3 and Bi0.92Dy0.08FeO3 ceramics were prepared to study their crystal structures and piezoelectric properties. BiFeO3 exhibits rhombohedral phase below 810°C. Although Bi0.92Dy0.08FeO3 ceramic also shows rhombohedral phase at room temperature, it allows the coexistence of rhombohedral phase and orthorhombic phase at 460–650°C. Both samples have maximum polarizations of >21μC/cm2 and piezoelectric d33 values of ∼37pC/N at room temperature. Their polarized slices show the dielectric anomalies and impedance anomalies because of vibrating resonances below 500°C, and the thickness vibration electromechanical coupling factor is ∼0.6 and ∼0.4 for BiFeO3 and Bi0.92Dy0.08FeO3, respectively. The vibrating resonances confirm piezoelectric responses. Furthermore, samples' impedance and resistance decrease fast with temperature increasing, which screens piezoelectric response above 550°C.