The Multiferroic Properties of Bi(Fe1/2cr1/2)O-3 Compound

J. L. Zhu,H. X. Yang,S. M. Feng,L. J. Wang,Q. Q. Liu,C. Q. Jin,X. H. Wang,L. T. Li,J. Yu
DOI: https://doi.org/10.1142/s0217979213620233
2013-01-01
International Journal of Modern Physics B
Abstract:Dense Bi ( Fe 1/2 Cr 1/2) O 3 ceramics with R3c crystal structure were synthesized by solid-state reaction under high pressure. Transmission electron microscope observations revealed an incommensurable superstructure along 〈110〉 direction. Magnetization measurements indicated a transition to a cooperative magnetic state below ~130 K. Dielectric properties of Bi ( Fe 1/2 Cr 1/2) O 3 showed a dielectric constant anomaly located at ~140 K indicating the giant dielectric relaxation in multiferroic Bi ( Fe 1/2 Cr 1/2) O 3 compound, which can be explained by the enhanced conductivity and possible Maxwell–Wagner contribution. Large dielectric frequency dispersion was observed at 140–185 K, and was supposed to be a thermal activated intrinsic process.