Abstract:Al2O3-ZrO(2)microspheres were prepared by internal gelation method. The effects of Al(3+)on the stability of solution and performance of gel spheres were studied. Al(3+)had a great influence on the stability of the solutions, and the more of the amount of Al3+, the shorter of the stabilization time. Because Al(3+)did not copolymerize with Zr(4+)during the sol-gel transformation, the strength of gel sphere added with Al(3+)was low and deformed easily as it was squeezed. The results of our experiments well verify Glasser team's speculation and conclusions. At the same time, based on the experimental results, we prepared Al2O3-ZrO(2)composite microspheres with higher content of Al(2)O(3)by controlling the pH of the solution. The change curve of viscosity with time and the stabilization time of the solution with different Al(3+)dosage were given, which could provide references for industrial mass production. Samples without hydrothermal treatment cracked severely, while the samples hydrothermally treated kept structural integrity with no cracks after calcined. Al2O3-ZrO(2)microspheres with no segregation and phase separation were prepared and alumina evenly distributed in the zirconia matrix. When the content of Al(2)O(3)was low, the tetragonal phase was stable. And the cubic phase was obtained when the content of Al(2)O(3)was more.

Effect of Ploy-Hollow Sphere on Performance of Al_2O_3 Ceramics

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

A New Al 2 O 3 Porous Ceramic Prepared by Addition of Hollow Spheres

A Novel Way to Prepare Hollow Sphere Ceramics

Preparation of Al 2 O 3 poly-hollow microsphere (PHM) ceramics using Al 2 O 3 PHMs coated with sintering additive via co-precipitation method

Enhancing thermal insulation and mechanical strength of porous ceramic through size-graded MA Hollow Spheres

Phase Evolution and Properties of Novel Al2O3-based Poly-Hollow Microsphere (PHM) Ceramics

Fabrication of Porous Al2TiO5-Al2O3 Ceramics Using Al2O3 Hollow Spheres Coated with TiO2 Sol

Preparation of porous Al2O3 ceramics with enhanced properties by SLS using Al2O3 poly-hollow microspheres (PHMs) coated with CaSiO3 sintering additive

Preparation of high-strength porous mullite ceramics and the effect of hollow sphere particle size on microstructure and properties

Influence of Y2O3 contents on sintering and mechanical properties of B4C-Al2O3 multiphase ceramic composites

Microstructure and Mechanical Properties of Porous Alumina Ceramics Fabricated by the Decomposition of Aluminum Hydroxide

Effect Of Talc And Titania On The Microstructure And Mechanical Properties Of Alumina Ceramics

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Effect of Al2O3on the Process Performance of ZrO2Microspheres

Effect of Alumina Fiber Content on Pore Structure and Properties of Porous Ceramics

Preparation and Properties of Hollow Ceramic Spheres-Epoxy Dielectric Composites

The Fabrication of Porous Mullite Ceramics Based on the Different Sizes of Aluminum Hydroxide

Al 2 O 3 -fiber-reinforced porous YSZ ceramics with high mechanical strength

Effect of Calcining Temperature of Si3N4 Poly-Hollow Microspheres on the Properties of the Porous Si3N4 Ceramics Prepared by Aqueous Gelcasting

Selective laser sintering of porous Al2O3-based ceramics using both Al2O3 and SiO2 poly-hollow microspheres as raw materials