Abstract:Extrusion-free-form printing of alumina ceramics has the advantages of low cost, short cycle time, and high customization. However, some problems exist, such as the low solid content of ceramic paste and the unsatisfactory mechanical properties of pure alumina ceramics. In this study, SiC nanoparticles were used as a reinforcement phase added to the alumina ceramic matrix. Methylcellulose is used as the binder in the raw material system. Ammonium polyacrylate is used as a dispersant to change the rheological properties of the slurry and increase the solid content of ceramics. SiC nanoparticle-strengthened alumina ceramics were successfully prepared by the extrusion process. The relative settling height and viscosity of ceramic slurries were characterized. The sintering shrinkage of composite ceramics was tested. The flexural strength, fracture toughness, and hardness of the ceramics were characterized. The strengthening and toughening mechanisms of the composite ceramics were further explained by microscopic morphology analysis. Experimental results show that when the content of the dispersant is 1 wt.%, the rheological properties of the slurry are the best. Maximum measured bending strength (227 MPa) and fracture toughness (5.35 MPa·m1/2) were reached by adding 8 wt% SiC nanoparticles; compared with pure alumina ceramics, flexural strength and fracture toughness increased by 42% and 41%, respectively. This study provides a low-cost and effective method for preparing ceramic composite parts.

Preparation of Al 2 O 3 poly-hollow microsphere (PHM) ceramics using Al 2 O 3 PHMs coated with sintering additive via co-precipitation method

Preparation of porous Al2O3 ceramics with enhanced properties by SLS using Al2O3 poly-hollow microspheres (PHMs) coated with CaSiO3 sintering additive

Phase Evolution and Properties of Novel Al2O3-based Poly-Hollow Microsphere (PHM) Ceramics

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Influence of CaO content by mass in sintering aid and sintering temperature on the properties of Al2O3-based microwave ceramic materials

Selective laser sintering of porous Al2O3-based ceramics using both Al2O3 and SiO2 poly-hollow microspheres as raw materials

Pore Morphology Designs of Porous Si3n4-Based Ceramics Using Si3n4 and Al2o3 Poly-Hollow Microspheres As Pore-Forming Agents

A New Al 2 O 3 Porous Ceramic Prepared by Addition of Hollow Spheres

Preparation of porous Si 3 N 4 ceramics via tailoring solid loading of Si 3 N 4 slurry and Si 3 N 4 poly-hollow microsphere content

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Fabrication of Porous Al2TiO5-Al2O3 Ceramics Using Al2O3 Hollow Spheres Coated with TiO2 Sol

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Effect of Ploy-Hollow Sphere on Performance of Al_2O_3 Ceramics

Effect of Al(OH)<sub>3</sub> Addition on the Properties of SiC/Al<sub>2</sub>O<sub>3</sub> Composite Porous Ceramics

Preparation of calcium hexaluminate porous ceramics by gel-casting method with polymethyl methacrylate as pore-forming agent

Effects of Composite Sintering Additives: Al(OH)3+Y2O3+CaF2 on the Performance of Porous Mullite Oxide-Bonded SiC Ceramics

A Novel Way to Prepare Hollow Sphere Ceramics

Effect of Al2O3 and TiO2 Addition Amount on Properties of MgO-based Ceramics by Coprecipitation Method

Significantly improved mechanical properties of mullite ceramics by adding AlOOH with different sizes and morphologies

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

Influence of Y2O3 contents on sintering and mechanical properties of B4C-Al2O3 multiphase ceramic composites