Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure and mechanical properties of the Mg-Gd-Y-Zn-Zr alloy fabricated by semi-continuous casting

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-4.50zn-1.13ca (wt%) Alloys

Microstructure and Mechanical Properties of Mg–3.0Y–2.5Nd–1.0Gd–x Zn–0.5Zr Alloys Produced by Metallic and Sand Mold Casting

Effect of Gd Content on Microstructure and Mechanical Properties of Mg-xGd-Zr Alloys Via Semicontinuous Casting

Microstructure and Mechanical Properties of Mg–Zn–Ca–Ce Alloy Processed by Semi-Continuous Casting

Microstructure and Properties of Semi-continuous Casting Mg-8Gd-3Y-0 .5zr Alloy

Microstructure evolution and mechanical properties of an ultra-high strength casting Mg–15.6Gd–1.8Ag–0.4Zr alloy

Microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy prepared by rheo-diecasting

The Partial Substitution of Y with Gd on Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-10Zn-6Y-0.5Zr Alloy

Microstructure and mechanical properties of Mg-12Gd-5Y-1Sm-0.5Zr alloy

Microstructures and mechanical properties of as-cast Mg–5Y–3Nd–Zr–xGd (x=0, 2 and 4wt.%) alloys

Microstructure and Mechanical Properties of Semi-Solid Die Casting Mg–5Zn–2Gd–0.6Zr Alloy

Microstructure and properties of Mg-9Gd-4Y-1Zn-0.5Zr alloy

Effect of Zn/(Gd+Y) ratio on the microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy

Mechanical properties and microstructure of a high-quality Mg-Nd alloy ingot with large size manufactured by direct chill casting

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Comparison of Microstructure in Mg–10Y–5Gd–0.5Zr and Mg–10Y–5Gd–2Zn–0.5Zr Alloys by Conventional Casting

Microstructural evolution and enhanced mechanical properties of Mg–Gd–Y–Zn–Zr alloy via centrifugal casting, ring-rolling and aging