Abstract:Polycarbosilane (PCS) serves as a crucial precursor for silicon carbide (SiC) fibers and ceramics. However, both of the precursor and the resulting SiC ceramics are carbon-rich, which is often viewed as detrimental to their relevant high-temperature properties. In this work, PCS is modified using nanosized Si particles to improve SiC grain growth and reduce carbon content in the resulting SiC ceramics, and the structural evolution during the polymer–ceramic conversion process has been meticulously investigated. The findings reveal that the incorporation of nano-Si into PCS raises its actual ceramic yield and accelerates the organic-inorganic conversion process. This is attributed to the formation of a more crosslinked structure at 200 °C–350 °C, resulting from the reaction between the Si–OH groups in nanosized Si and the Si–H and Si–CH3 groups in PCS. The carbothermic reaction between nano-Si and the free carbon starts at approximately 1200 °C at the periphery of nanosized Si particles, and is accomplished at around 1400 °C. This leads to the formation of large-sized reactive β-SiC. Simultaneously, PCS-derived β-SiC with smaller sizes is also formed at 1300 °C–1400 °C. At 1600 °C–1800 °C, the growth of the reactive and the derived β-SiC in nano-Si-modified PCS is both accelerated due to a substantial decrease in the free carbon content. Consequently, the grain size of β-SiC is much larger than that of unmodified PCS. Additionally, the residual amorphous free carbon transforms into nanocrystalline carbon at around 1400 °C and evolves into graphite carbon at 1600 °C–1800 °C, which exhibits a more ordered structure with larger size compared to that in unmodified PCS.

Thermally Curable Poly(silylacetylene)siloxane As Polymeric Precursor of SiC Ceramic

Preceramic Polymer As Precursor for Near‐stoichiometric Silicon Carbon with High Ceramic Yield

Preparation of SiC ceramic fiber from a photosensitive polycarbosilane

Synthesis of cyano-polycarbosilane and investigation of its pyrolysis process

Polymethylsilane As A Precursor to High-Purity Silicon-Carbide

C/C–SiC Composites Derived from Single‐source Poly(silylene–acetylene) Precursors

A linear polycarbosilane containing <i>m</i>-carborane units: Synthesis and characterization as precursor for SiC/B<sub>4</sub>C ceramics

A linear polycarbosilane containing m-carborane units: Synthesis and characterization as precursor for SiC/B4C ceramics

Preparation and Stereolithography of SiC Ceramic Precursor with High Photosensitivity and Ceramic Yield

Evaluation of Poly(methylsilane‐carbosilane) Synthesized from Methyl‐dichlorosilane and Chloromethyldichloromethylsilane As a Precursor for SiC

Preparation of liquid polycarbosilane containing vinyl ether group and its rapid curing through thiol‐ene click reaction

Digital light processing of SiC ceramic from allylhydridopolycarbosilane with limited acrylate monomers

Synthesis and Characterization of Poly[(Methylsilylene Ethynylenephenyleneethynylene)-Co-(Dimethylsilylene Ethynylenephenyleneethynylene)]S

Polymerization of polycarbosilanes in high internal phase emulsions for the synthesis of macroporous silicon carbide catalysts (polyHIPE-SiC)

A Pyrolysis Heating Rate Based Pressureless Method for Preparing Dense and Crack-Free Polymer-Derived Silicon Oxycarbide Bulk Ceramics

A New SiC Precursor with High Ceramic Yield: Synthesis and Characterization of CHxMeSiH2‐containing Poly(methylsilane‐carbosilane)

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Synthesis and characteristics of polycarbomethylsilane via a one-pot approach

The Preparation Process Of Sicn Ceramic By Pyrolysis Of Psn-1

Reaction-bonded SiC Derived from Resin Precursors by Stereolithography

Synthesis, Characterization and Oxidation Behavior of A Novel Curable Liquid Polysilane Precursors for C/C-Sic Composite