Abstract:A series of wholly aromatic hyperbranched polyimides were successfully prepared by condensation polymerization of a triamine monomer, tris(4-aminophenyl)amine (TAPA), and a series of commercially available dianhydride monomers such as 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA), 3,3',4,4'-diphenylsulfonetetracarboxylic dianhydride (DSDA), and pyromellitic anhydride (PMDA). The synthesis involves the formation of hyperbranched polyamic acid precursors in the first step and the thermal or chemical imidization in the subsequent step, which is similar to the conventional two-step method for the synthesis of linear polyimides. Different monomer addition orders resulted in different hyperbranched polymers even if the same kinds of monomers but different molar ratios were used. When a dianhydride solution was added to the TAPA solution (manner 1), an amine-terminated hyperbranched polyimide was obtained, whereas the addition of TAPA solution to a dianhydride solution (manner 2) yielded an anhydride-terminated hyperbranched polyimide. The appropriate molar ratios of TAPA to a dianhydride are 1:1 for manner 1 and 1:2 for manner 2. From H-1 NMR spectra the branching degrees of the amine-terminated hyperbranched polyimides were estimated to be 0.64, 0.72, and 0.68 for 6FDA-TAPA, DSDA-TAPA, and PMDA-TAPA, respectively. All the anhydride-terminated polyimides were found wholly branched. Gel permeation chromatography (GPC) measurement revealed that both the amine-terminated and anhydride-terminated 6FDA-TAPA polyimides had moderate number-averaged molecular weights, but the latter had very broad molecular weight distribution.

Synthesis and Properties of Hyperbranched Polyimides from A2+ B′B2 Monomers and A2+ B′B2 + B2 Monomers with Various Comonomer Ratios

Synthesis and Characterization of Hyperbranched Polyimides from a Novel B ' B-2-type Triamine with Tert-Butyl Side Group

Synthesis and Properties of Hyperbranched Polybenzimidazoles Via A(2)+B-3 Approach

Preparation and Properties of Novel Triphenylpyridine‐Containing Hyperbranched Polyimides Derived from 2,4,6‐tris(4‐aminophenyl)pyridine under Microwave Irradiation

Hyperbranched Polyimides for Gas Separation Applications. 1. Synthesis and Characterization

Synthesis, characterisation and thermal properties of hyperbranched polyimide derived from melamine via emulsion polymerisation

Preparation and Characterization of Hyperbranched Polyaspartimides from Bismaleimides and Triamines

Synthesis and Properties of Highly Soluble Branched Polyimide Based on 2,4,6-Triaminopyrimidine

Synthesis and Properties of Some New Polyimides Containing Bithiazole Rings

Synthesis And Characterization Of Hyperbranched Polyurethanes Via Monomeric A2 Plus Monomeric B3 Approach

Synthesis and Characterization of Biphenyl Polyimide Containing Alkyl Sulfide Structure

Synthesis, Freestanding Membrane Formation, and Properties of Novel Sulfonated Hyperbranched Polyimides

Study on Syntheses and Properties of Some Novel Polyimides Containing Bisthiazole Rings

Synthesis of Hyperbranched Polybenzimidazoles and Their Membrane Formation

Hyperbranched Copolymers Made from A 2 , B 2 and BB′ 2 Type Monomers (Iv)

Hyperbranched copolymers made from A2, B2 and BB′2type monomers (iv): Copolymerization of divinyl sulfone with 4, 4′-trimethylenedipiperidine and N-ethylethylenediamine

Synthesis and Properties of Hyperbranched Aqueous Poly(urethane–urea) Via A2 + Bb2 Approach

Synthesis and Characterization of Soluble Polyimides Containing Tert-Butyl, Ether Linkages and Bisphenol A Units

Hyperbranched Copolymers Made from A2, B2 and BB′2 Type Monomers, 3. Comparison of Copoly(sulfone-amine)s Containing Piperazine and 4,4′-Trimethylenedipiperidine Units

Synthesis and themo property of poly(aryl imino) containing biphenyl group

Synthesis and Characterization of Polyimides Derived from 5-Amino-2(p-aminophenyl) Benzoxazole Monomer