Abstract:In this study, a series of novel contorted hyberbranched polyimides (HBPIs) were successfully prepared based on commercially available monomers 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6FDA), 1,1′-binaphthyl- 2,2′-diamine (BNDA), and 1,3,5-tris(4-aminophenyl) benzene (TAPB), and the BNDA comonomer was used to create the contorted moieties in polymer backbone. Experimental results demonstrated that all the prepared HBPIs possessed high glass transition temperatures (Tg = 309~325 °C), excellent thermal stability (Td,5% = 489~503 °C), and their PAA precursors had high number-averaged molecular weights (Mn = 2.9 × 104~5.6 × 104 g/mol). Furthermore, the effect of the degree of contorted moieties in HBPIs changing by the different molar ratios of TAPB:BNDA on polymeric fractional free volumes (FFV) and gas transport properties was systematically investigated. As a result, with the increasing content of BNDA monomer, the gas permeabilities of HBPI membranes were significantly increased. For example, the CO2 and O2 permeabilities of HBPI membrane with the molar ratio of TAPB:BNDA = 4:6 were respectively about 2.8 and 3.2 times higher than that of HBPI membrane without any contorted moieties. Besides, it also maintained reasonable selectivities for CO2/CH4 (~46.3) and O2/N2 (~5.7). These encouraging results were related to the synergetic effects of incorporating contorted sites and improving polymer rigidity by using monomers BNDA and TAPB in copolymerization reaction. Furthermore, no gelation occurred during polymerizations due to the adopted low-temperature synthesis technique that can effectively avoid the high local concentration of the added 6FDA monomer. This work provides a new insight to produce high performance contorted HBPIs containing binaphthyl structures without risk of gelation and also shows a potential application in gas separation.

Synthesis, Freestanding Membrane Formation, and Properties of Novel Sulfonated Hyperbranched Polyimides

Benzimidazole Grafted Polybenzimidazole Cross-Linked Membranes with Excellent PA Stability for High-Temperature Proton Exchange Membrane Applications

Sulfonated Polyaryletherketone with Pendant Benzimidazole Groups for Proton Exchange Membranes

Synthesis and Characterization of Photocrosslinked Biobased Polyester Membrane

Ethyl Phosphoric Acid Grafted Amino-Modified Polybenzimidazole with Improved Long-Term Stability for High-Temperature Proton Exchange Membrane Applications

Novel Sulfonated Polyimides Proton-Exchange Membranes Via a Facile Polyacylation Approach of Imide Monomers

Study on Syntheses and Properties of Some Novel Polyimides Containing Bisthiazole Rings

Synthesis and Properties of Some New Polyimides Containing Bithiazole Rings

A novel cross-linked anion exchange membrane with conjugated and non-conjugated pyridine groups

Synthesis of novel membranes of polyimide with side-chains and their pervaporation performance

Polyhedral oligosilsesquioxane-modified boron nitride enhances the mechanical properties of polyimide nanocomposites

Synthesis and Characterization of Biphenyl Polyimide Containing Alkyl Sulfide Structure

Preparation and Properties of Novel Triphenylpyridine‐Containing Hyperbranched Polyimides Derived from 2,4,6‐tris(4‐aminophenyl)pyridine under Microwave Irradiation

Synthesis and Characterization of Novel Fluorinated Polyimides Derived from 4-Phenyl-2,6-bis[4-(4′-amino-2′-trifluoromethyl-phenoxy)phenyl]pyridine and Dianhydrides

Synthesis and properties of polyimides from a diamine containing side diphenylphosphine oxide and trifluoromethyl groups

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Synthesis of Furan-Based Diamine and Its Application in the Preparation of Bio-Based Polyimide

Low-temperature synthesis and gas transport properties of novel contorted hyperbranched polyimides containing binaphthyl structures

Exploration of Antifouling Zwitterionic Polyimide Ultrafiltration Membrane Based on Novel Aromatic Diamine Monomer

Synthesis and gas separation performances of intrinsically microporous polyimides based on 4-methylcatechol-derived monomers

Novel Synthesis of Polyimide Foams with Aromatic and 1,6-Diaminohexane Imide Bonding