Abstract:A series of wholly aromatic hyperbranched polyimides were successfully prepared by condensation polymerization of a triamine monomer, tris(4-aminophenyl)amine (TAPA), and a series of commercially available dianhydride monomers such as 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride (6FDA), 3,3',4,4'-diphenylsulfonetetracarboxylic dianhydride (DSDA), and pyromellitic anhydride (PMDA). The synthesis involves the formation of hyperbranched polyamic acid precursors in the first step and the thermal or chemical imidization in the subsequent step, which is similar to the conventional two-step method for the synthesis of linear polyimides. Different monomer addition orders resulted in different hyperbranched polymers even if the same kinds of monomers but different molar ratios were used. When a dianhydride solution was added to the TAPA solution (manner 1), an amine-terminated hyperbranched polyimide was obtained, whereas the addition of TAPA solution to a dianhydride solution (manner 2) yielded an anhydride-terminated hyperbranched polyimide. The appropriate molar ratios of TAPA to a dianhydride are 1:1 for manner 1 and 1:2 for manner 2. From H-1 NMR spectra the branching degrees of the amine-terminated hyperbranched polyimides were estimated to be 0.64, 0.72, and 0.68 for 6FDA-TAPA, DSDA-TAPA, and PMDA-TAPA, respectively. All the anhydride-terminated polyimides were found wholly branched. Gel permeation chromatography (GPC) measurement revealed that both the amine-terminated and anhydride-terminated 6FDA-TAPA polyimides had moderate number-averaged molecular weights, but the latter had very broad molecular weight distribution.

Synthesis and Characterization of Hyperbranched Polyimides from a Novel B ' B-2-type Triamine with Tert-Butyl Side Group

Synthesis and characterization of hyperbranched polyacrylamide using semibatch reversible addition-fragmentation chain transfer (RAFT) polymerization

Preparation and Properties of Novel Triphenylpyridine‐Containing Hyperbranched Polyimides Derived from 2,4,6‐tris(4‐aminophenyl)pyridine under Microwave Irradiation

Preparation and Characterization of Hyperbranched Polyaspartimides from Bismaleimides and Triamines

Synthesis and Properties of Hyperbranched Polybenzimidazoles Via A(2)+B-3 Approach

Synthesis and Characterization of Hyperbranched Polytriazole Via an 'A(2)+ B-3' Approach Based on Click Chemistry

A Novel Hyperbranched Polyester Made from Aconitic Acid (B3) and Di(ethylene Glycol) (A2)

A Novel Hyperbranched Copolymer Constituted of Triphenylamine and Divinyl Bipyridyl Units

Synthesis and Charaterization of Hyperbranched Poly(amine-ester)

Two step synthesis of hydroxyl group polyimide based on 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane

Synthesis And Characterization Of Hyperbranched Polyurethanes Via Monomeric A2 Plus Monomeric B3 Approach

Two Step Synthesis of Hydroxyl Group Polyimide Based on 2,2-Bis(amino-4-hydroxyphenyl)hexafluoropropane

Synthesis of Hyperbranched Polyenediynes with Maleimide Moieties

Hyperbranched Polyimides for Gas Separation Applications. 1. Synthesis and Characterization

Synthesis, characterisation and thermal properties of hyperbranched polyimide derived from melamine via emulsion polymerisation

Synthesis and themo property of poly(aryl imino) containing biphenyl group

Synthesis of Hyperbranched Polybenzimidazoles and Their Membrane Formation

Synthesis and Characterization of Soluble Polyimides Containing Tert-Butyl, Ether Linkages and Bisphenol A Units

Hyperbranched copolymers made from A2, B2 and BB′2type monomers (iv): Copolymerization of divinyl sulfone with 4, 4′-trimethylenedipiperidine and N-ethylethylenediamine

Synthesis, Freestanding Membrane Formation, and Properties of Novel Sulfonated Hyperbranched Polyimides

Hyperbranched Copolymers Made from A 2 , B 2 and BB′ 2 Type Monomers (Iv)