Microstructural Control of TiAl–Nb Alloys by Directional Solidification

X. F. Ding,J. P. Lin,L. Q. Zhang,Y. Q. Su,G. L. Chen

DOI: https://doi.org/10.1016/j.actamat.2011.10.009

IF: 9.4

2012-01-01

Acta Materialia

Abstract:The lamellar microstructure of TiAl–Nb alloys with and without low boron additions is controlled using double directional solidification (DS). In alloys without the addition of boron, the β phase is seeded during double DS. Complete peritectic transformation occurs in both the dendritic and interdendritic regions, which can lead to the successful alignment of both the high-temperature α phase and the lamellar microstructures. Well-aligned lamellar microstructures can be easily achieved if the alloy composition is close to the peritectic point on the hypo-peritectic side. In alloys with low boron additions, however, the competitive growth of the α phase breaks the continuity of the lamellar microstructure in the region ahead of stable growth, which finally results in columnar grain coarsening and unsuccessful alignment of the lamellar microstructures.