Microstructure Evolution and Simulation of Solidification Path in Nb10Ti61Co29 Quasi-peritectic Alloy
Di Chongbo,Yan Erhu,Chen Yuncan,Wang Jinhua,Liu Wei,Wang Hao,Sun Lixian
2021-01-01
Rare Metal Materials and Engineering
Abstract:The Nb10Ti61Co29 alloy near the quasi-peritectic point was selected as the research object in this paper, and a series of directional solidification experiments with different growth rates (v=1, 3, 5, 15, 30, 70 mu m/s) were carried out by Bridgman directional solidification technique. Then the solidification structure at each growth rate was analyzed by XRD, SEM and EDS, and the microstructure evolution law of these directionally solidified samples was clarified. The results show that the solidification structure of this alloy at different growth rates includes initial transition zone, steady-state growth zone and quenching zone. As the growth rate increases, the profile of the initial growth interface in the initial transition zone becomes more and more clear. With these changes, the relationship between the steady-state growth region and the initial transition region gradually becomes smaller. Moreover, the quenching interfaces undergoes the transformation from flat-bound to cell-oriented to dendrite in turn with the increase of the growth rate. Especially, the quenching interface is flat when the growth rate is 1 mu m/s, whereas the quenching interface is roughly cellular when the growth rates are 3 and/or 5 mu m/s. Lastly, the following four solidification reactions will occur successively in the process of equilibrium solidification, which was calculated by C ALPHAD method, (a) L ->alpha-Nb; (b) binary eutectic reaction L ->alpha-Nb+TiCo; (c) ternary quasi-peritectic coated reaction L+TiCo ->alpha-Nb+Ti2Co and (d) binary eutectic reaction L ->alpha-Nb+Ti2Co.