Evolution Law of Directional Solidification Structure for Nb<sub>42</sub>Ti<sub>21</sub>Co<sub>37</sub> Ternary Quasi-peritectic Alloy
Wang Jinhua,Yan Erhu,Di Chongbo,Chen Yuncan,Liu Wei,Wang Hao,Ge Xiaoyu,Cheng Jian,Huang Renjun,Sun Lixian
2021-01-01
Rare Metal Materials and Engineering
Abstract:The quasi-peritectic transformation, which has the dual characteristics of eutectic and peritectic reaction, exists in many industrial alloys. However, a relatively complete theoretical model of this transformation has not been established so far, and there are few related studies on its solidification mechanism. Given this, the directional solidification experiments at different drawing speeds (V=1, 3, 5, 15, 30, 70 mu m/s) for the Nb47Ti21Co37 quasi-peritectic alloy were carried out, aiming to study the evolution law of directional solidification structure at different speeds and explore the corresponding solidification mechanism. The results show that the a-Nb, Co6Nb7 and TiCo+Co6Nb7 quasi-peritectic phases exist in the conventional as-cast and directional solidification structures of Nb47Ti21Co37 quasi-peritectic alloy. With the gradual increase of the drawing speed, the primary a-Nb phase undergoes a transformation of spherical shape -> petal-like -> cluster-like -> dendrite-like. During the above process, the quenched interface undergoes the transformation from cellular-like interface to cellular dendrite-like interface, and the corresponding solid/liquid interface disappears when the drawing speed is equal to 70 mu m/s. Secondly, the quasi-peritectic structure in the steady-state growth zone of directional solidification gradually refines, and an exponential linear relationship of the quasi-peritectic interphase spacing versus the drawing speed, i.e. lambda=1+5e(2.5v), appears for the directionally solidified samples. When the drawing speed is lower than 5 mu m/s, the directional solidification process is near-equilibrium conditions, and the growth mechanism of each phase in the stable growth zone is symbiotic growth. With the increase of the drawing speed, the directional arrangement of the quasi-peritectic structure gradually deteriorates.