Abstract:Since temperatures of airfoil surfaces in advanced turbine engines are approaching the limit of nickel base superalloys, Nb-Ti-Si base alloys as their potential materials have attracted much attention recently. Nb-Ti-Si base alloys have high melting temperature, suitable densities, good elevated temperature creep strength and acceptable room temperature fracture toughness, therefore, they are expected to be employed in the temperature range of 1200-1450 ℃ as structural materials. Alloying and directional solidification are generally used to obtain a better combination of room temperature fracture toughness with high temperature creep strength and oxidation resistance for an elevated-temperature alloy. In this paper, the master alloy ingot with a nominal composition of Nb20Ti-16Si-6Cr-5Hf-4Al-2B-0.06Y (atomic fraction, %) was prepared by using vacuum consumable arc-melting. The integrally directional solidification of this alloy was conducted in a high vacuum and ultrahigh temperature directional solidification furnace with the use of a ceramic crucible at melt temperature of 2050 ℃. The integrally directionally solidified microstructure, preferred orientation of constituent phases and solid/liquid (S/L) interface morphology at different solidifying rate (2.5, 5, 10,20, 50 and 100 μm/s) for this alloy have been investigated by XRD, SEM and EDS, and the growth mechanism of Nbss/(Nb, X)_5Si_3 (where Nbss denotes Nb solid solution, X represents Ti, Hf and Cr elements) eutectic in it has been discussed. The results show that the directionally solidified microstructure of the alloy is mainly composed of hexagonally cross-sectioned primary (Nb, X)_5Si_3 columns and coupled grown lamellar Nbss/(Nb, X)_5Si_3 eutectic colonies both aligned straight and uprightly along the growth direction. When the solidifying rate varies from 2.5 μm/s to 100 μm/s, the solid/liquid interface of the alloy undergoes an evolution from coarse cellular, fine cellular and finally to cellular dendrite morphologies. Both the average diameter of eutectic cells and lamellar spacing in them decrease with the increase in solidifying rate. The formation of a regular Nbss/(Nb, X)_5Si_3 eutectic morphology is attributable to a large kinetic undercooling and a low fusion entropies of alloy phases.

Microstructure Development of Directionally Solidified Nb-Ti-Si Based Ultrahigh Temperature Alloy

Microstructure of Nb–Ti–Cr–Si Based Ultrahigh Temperature Alloy Processed by Integrally Directional Solidification

Microstructural Characteristics of Integrally Directionally Solidified Nb-Ti-Sibase Ultrahigh Temperature Alloy with Crucibles

INTEGRALLY DIRECTIONALLY SOLIDIFIED MICROSTRUCTURE OF AN NIOBIUM SILICIDE BASED ULTRAHIGH TEMPERATURE ALLOY

MICROSTRUCTURE AND SOLID/LIQUID INTERFACE MORPHOLOGY EVOLUTION OF INTEGRALLY DIRECTIONALLY SOLIDIFIED Nb-SILICIDE-BASED ULTRAHIGH TEMPERATURE ALLOY

Eutectic Microstructure Evolution of Directionally Solidified Nb-Ti-Si Base Ultrahigh Temperature Alloy

Microstructure evolution and room temperature fracture toughness of an integrally directionally solidified Nb–Ti–Si based ultrahigh temperature alloy

DIRECTIONALLY SOLIDIFIED MICROSTRUCTURE OF AN ULTRA-HIGH TEMPERATURE Nb-Si-Ti-Hf-Cr-Al ALLOY

Microstructure and microhardness of directionally solidified and heat-treated Nb-Ti-Si based ultrahigh temperature alloy

EFFECT OF SOLIDIFYING RATE ON INTEGRALLY DIRECTIONALLY SOLIDIFIED MICROSTRUCTURE AND SOLID/LIQUID INTERFACE MORPHOLOGY OF AN Nb-Ti-Si BASE ALLOY

Microstructure and room temperature fracture toughness of directionally solidified Nb-Ti-Si based ultrahigh temperature alloy

Effects of Heat Treatments on the Microstructure and Microhardness of Directionally Solidified Nb-Ti-Si Based Ultrahigh Temperature Alloy

Effect of Withdrawal Rates on Microstructures and Room Temperature Fracture Toughness in a Directionally Solidified Nb–Ti–Cr–Si Based Alloy

Effect of Heat-Treatment on Microstructure and Mechanical Behavior of Directionally Solidified Nb-Ti-Si Based Alloy

Microstructures and mechanical properties of directionally solidified multi-element Nb-Si alloy

Microstructure Evolution of a Hypereutectic Nb–Ti–Si–Cr–Al–Hf Alloy Processed by Directional Solidification

Microstructure Evolution of Eutectic Nb–24Ti–15Si–4Cr–2Al–2Hf Alloy Processed by Directional Solidification

Microstructure evolution and solidification behaviour of Nb–16Si–22Ti–2Cr–2Al–6Hf alloy processed by directional solidification

Microstructure and Mechanical Properties of Nb Based Ultrahigh Temperature Alloy Directionally Solidified by EBFZM

Eutectic Evolution of Directionally Solidified Nb-Si Based Ultrahigh Temperature Alloys

Research Progress in the Directionally Solidified Microstructure and the Eutectic Solidification Theory of Niobium-based Ultrahigh-temperature Alloy