Abstract:In this work, the influences of excess amount of sodium ions and the way/duration of ageing of the reaction mixture (hydrogel) on structural, particulate, morphological and chemical properties of the crystalline end products obtained by hydrothermal treatment (heating at 483K for 2h) of the TPA-free reaction mixture: 1.0Al2O3/100SiO2/xNa2O/4000H2O/yNa2SO4 (0.4⩽(x+y)⩽100) seeded by silicalite-1 nanocrystals (260nm, 4wt.% of silica in gel mixture), was investigated by different characterization methods such as, powder X-ray diffraction (XRD), scanning-electron microscopy (SEM), particle size distribution (PSD) measuring by laser light scattering (LLS) and X-ray fluorescence (XRF). The obtained results showed that addition of sodium sulfate in low-alkaline reaction mixture enhances the aggregation of the particles of colloidal silica and formation of gel by the action of sulfate oxy-anions while in high-alkaline reaction mixtures the condensation process takes place on the surface of the crystalline end products. Excess amount of sodium ions do not increase the crystallization rate thus showing that the rate-determining factor is concentration of “free” low-molecular weight silicate species, determined by the alkalinity of system. On the other hand, addition of sodium sulfate considerably reduces the formation of crystal aggregates, by combined chemical and electrical interactions. Ageing of the reaction mixture (hydrogel) mainly influences the particle size distribution of the crystalline end products, which is explained by the change in the relative rates of crystal growth and crystal aggregation with the time of ageing. However, hydrogel ageing does not affect the size and number of crystals in the crystalline end product, showing that the growth precursor particles form during hydrothermal treatment of the reaction mixture and not during its room-temperature ageing.

Synthesis of Al–Si-beta and Ti–Si-beta by the Aging–drying Method

Synthesis and Characterization of Pure Silica Zeolite Beta Obtained by an Aging–drying Method

Controllable and SDA-free synthesis of sub-micrometer sized zeolite ZSM-5. Part 2: Influence of sodium ions and ageing of the reaction mixture on the chemical composition, crystallinity and particulate properties of the products

Effect of the Aging Temperature of Gel on the Synthesis and Properties of the Silicoaluminophosphate Molecular Sieve SAPO-11

Synthesis of β Zeolite Using Tetraethylammonium Bromide Together with Fluoride as Composite of Template (II) - Studies on Crystallization Process of β Zeolite

Static synthesis of high-quality MCM-22 zeolite with high SiO 2 /Al 2 O 3 ratio

Study on the Structure Characterized and the Process of Thermal Decomposition of Beta Zeolite Synthesized by two Kind of Aluminum Sources

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Synthesis and structural characterization of SiO2-Al 2O3 xerogels

Regulating acidity, porosity, and morphology of hierarchical SAPO-11 zeolite by aging treatment

Direct Synthesis of Al−SBA-15 Mesoporous Materials Via Hydrolysis-Controlled Approach

Synthesis and Structural Characterization of SiO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub> Xerogels

The Role of Intermediate Phases in the Crystallization of Aluminophosphate Sieves on Examples of AlPO-11 and AlPO-41

The Synthesis and Characterization of SiO_2-Al_2O_3 Xerogels

Synthesis and characterization of β zeolite from aluminosilicate sol containing fluorion

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Tetrapropylammonium Hydroxide Treatment of Aged Dry Gel to Make Hierarchical TS-1 Zeolites for Catalysis

Al2O3 XEROGELS SYNTHESIZED BY INORGANIC SALT AND ORGANIC ALKOXIDE

Effect of Aluminum Doping on the Performance and Microstructure of Methyl-Modified SiO2 Sol

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure