Abstract:The non-contact electrical resistivity method was employed to investigate the microstructural development of three grades of cement under a fixed water-to-cement ratio (w/c) and the same curing conditions. The method was verified by measuring the heat of hydration and estimating the degree of hydration of the three pastes. The results showed that the existence of a linear relationship between the compressive strength at 28 d (f 28) and bulk electrical resistivity at 72 h (ρ72); thus, the proposed method can be used to assess the strength of cement. Moreover, the results indicated that the quality of cement can be further distinguished by interpreting the trend in the resistivity curve. The high-strength cement will have lower electrical resistivity values during cement dissolution due to the higher content of ions in the pore solution, while it will have higher resistivity values during cement hardening due to the greater amount of hydrates. The electrical resistivity of the cement solution (ρ0) filtered from the cement paste at an early age was measured to demonstrate the effect of the ionic concentration on the bulk electrical resistivity in the initial hydration period. The measured liquid resistivity of cement can be used as an indication of clinker reactivity; higher-strength cement will always have lower measured values. The rate of electrical resistivity development curve was plotted to elucidate the setting range of cement pastes based on three critical points. The time at the second critical point (C2) coincided with the final setting time determined using a Vicat needle. New general relationships between the gel-space ratio and electrical resistivity were developed. Furthermore, autogenous shrinkage was measured for the three cement pastes, and the behaviour could be anticipated from the electrical resistivity measurements.

Observation of Microstructure Formation Process of Cement Paste Using Non-Destructive Methods

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

In Situ Continuously Monitoring the Early Age Microstructure Evolution of Cementitious Materials Using Ultrasonic Measurement

Solid Phases Percolation and Capillary Pores Depercolation in Hydrating Cement Pastes

Resistivity Method for Monitoring the Early Age Pore Structure Evolution of Cement Paste

Nondestructive Monitoring the Deterioration Process of Cement Paste Exposed to Sodium Sulfate Solution by X-ray Computed Tomography

Continuous Tracking of the Relationship Between Resistivity and Pore Structure of Cement Pastes

Electrochemical Impedance Spectroscopy Monitoring of Hydration Behaviors of Cement with Na2CO3 Accelerator

In-situ Monitoring of Hydration Kinetics of Cement Pastes by Low-Field NMR

Continuous Characterization of Pore Structure in Cement Paste

Ultrasound Monitoring of Setting and Hardening Process of Ultra-High Performance Cementitious Materials

Ultrasonic monitoring of hydration behavior of cement paste doped with triethanolamine using novel piezoelectric ultrasonic transducer

Rheometric and ultrasonic investigations of viscoelastic properties of fresh Portland cement pastes

INTERPRETATION OF MICROSTRUCTURE DEVELOPMENT OF CEMENTITIOUS MATERIALS IN EARLY AGES WITH ELECTRICAL RESISTIVITY MEASUREMENT

Investigation of the Early-Age Microstructural Development of Hydrating Cement Pastes Through Electrical Resistivity Measurements

Portland Cement Hydration by Electrical Resistivity Method and Computer Simulation

Application of X-CT Technology in the Microstructure Analysis of Cement-Based Materials

Characterization of Microstructure and Specific Surface Area of Pores in Cement Paste by Low Field Nuclear Magnetic Resonance Technique

Evaluation of Microstructural Changes in Fresh Cement Paste Using AC Impedance Spectroscopy Vs. Oscillation Rheology and 1H NMR Relaxometry

Non-Destructive Characterization of Pore Structure and Chloride Diffusion Coefficient of Cementitious Materials with Modified Non-Contact Electrical Resistivity Method

A Micromechanical Investigation of Cement Paste Through a Combination of the X-ray Computed Tomography and the Phase Field Method