Abstract:Mineral admixtures (MA), like fly ash (FA), silica fume (SF), and slag (S), are usually added to cement-based materials to improve their compactness and further enhance their mechanical properties, permeability resistance, and durability. In this study, low-field nuclear magnetic resonance (LF-NMR) is adopted to explore the evolution of the early hydration characterization of cement-based materials with MA by testing the transverse relaxation time T2. Meanwhile, the effect of MA on mechanical properties is analyzed by measuring compressive and flexural strength. The results show that, in the early hydration (0–7 days), the T2 distribution shows a trend of gradually moving to a short relaxation time and changes from a double peak to a single main peak. The decrease in T2i (main peak vertex) means that the evaporated water is gradually distributed in smaller pores with more motion constraints. However, the type and content of MA have little effect on T2i. Porosity gradually decreases in the period of early hydration. The addition of MA causes the porosity to decrease, and the order influence is FA > S> SF, i.e., the porosities of cement paste with 0%MA, 10%FA + 10%SF, 10%FA + 10%S, and 20%FA at 7 days are 48%, 44.5%, 40.7%, and 40.2%, respectively. Additionally, the addition of MA to cement-based materials also decreases the early strength, and the influence order is FA > S> SF, i.e., the compression strength values of cement paste with 0%MA, 10%FA + 10%SF, 10%FA + 10%S, and 20%FA at 7 days are 47.8 MPa, 40.1 MPa, 38.6 MPa, and 37 MPa, respectively.

Characterization of Microstructure and Specific Surface Area of Pores in Cement Paste by Low Field Nuclear Magnetic Resonance Technique

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Pore Structure of Cement Pastes Through NAD and MIP Analysis

Characterizing Connectivity and Tortuosity of Pore Network Based on LF-NMR Method to Assess the Water Permeability of White Cement Mortar

Unveil the Role of Nano-Caco3 in Early Shrinkage and Tensile Properties of Cement Paste: from Experimental Work to Modeling

Experimental analysis on the relationship between pore structure and capillary water absorption characteristics of cement‐based materials

Application of Low-Field NMR to the Pore Structure of Concrete

Hydration of Early‐Age Composite Cement Paste Using Low‐Field Nuclear Magnetic Resonance

Pore structure characterization of cement paste by different experimental methods and its influence on permeability evaluation

Low-Field Nuclear Magnetic Resonance Investigation on Early Hydration Characterization of Cement Paste Mixed with Mineral Admixtures

An NMR-Based Experimental Study on the Pore Structure of the Hydration Process of Mine Filling Slurry

Pore structure characterization of cement pastes blended with high-volume fly-ash

Quantifying early age hydration and micro-structure evolution of fast setting binder using 1 H NMR

Pore Structure Damages In Cement-Based Materials By Mercury Intrusion: A Non-Destructive Assessment By X-Ray Computed Tomography

Pore Structure Characteristics and Its Effect on Mechanical Performance of Cemented Paste Backfill

The pore structure and water absorption in Portland/slag blended hardened cement paste determined by synchrotron X-ray microtomography and neutron radiography

Pore Structure Quantification and Fractal Characterization of MSA Mortar Based on 1H Low-Field NMR

Nanoindentation Characteristics of Cement Paste and Interfacial Transition Zone in Mortar with Rice Husk Ash

Effects of nano-C-S-H seed crystal on early-age hydration process of Portland cement

Insights into the effect of CNTs on cement hydration from the perspective of water evolution

Prediction of Effective Chloride Diffusivity of Cement Paste and Mortar from Microstructural Features