Preparation and Characterization of TiB2/Al3Ti/Al2O3 Composite Nano-powder
Ling-he Zeng,Kai Wang,Xiao-feng Zhen,Nianbing Zhang
DOI: https://doi.org/10.1007/s11837-024-06867-x
2024-10-04
JOM
Abstract:TiB 2 /Al 3 Ti/Al 2 O 3 composite nano-powder has been prepared by sintering TiO 2 , Al powder, and B 2 O 3 with molten salt as the medium. The sintered powder was characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy–energy dispersive spectroscopy (TEM–EDS), and x-ray photoelectron spectroscopy (XPS). The results illustrated the successful synthesis of TiB 2 /Al 3 Ti/Al 2 O 3 nano-powder when the mass ratio of molten salt to reactants was 3 after calcination at 1000°C for 3 h. The synthesized powder comprises baseball-like, lamellar, and spheroidal nanoparticles, with TiB 2 and Al 2 O 3 presenting a nano-scale mosaic structure which was used to reinforce aluminum-based composites. The synthesis mechanism of TiB 2 /Al 3 Ti/Al 2 O 3 nano-powder was also investigated. With the increase in temperature, Al 2 O 3 , Al 3 Ti, and Al 8 B 2 O 15 intermediate phases were first generated. Then, the further increase in temperature promoted the dissolution and diffusion of the unstable Al 8 B 2 O 15 phase in the molten salt, increasing the contact between Ti and B, thus producing the TiB 2 phase. By adding the TiB 2 /Al 3 Ti/Al 2 O 3 powder to the A6061 aluminum alloy at a 5% mass fraction, the Vickers hardness of the original alloy increased by 55.30%.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy