Abstract:Abstract GLARE laminates have emerged as a favored option for the construction of fuselage and wing skins in large airliners, owing to their exceptional mechanical characteristics. Nevertheless, the incorporation of open‐hole designs poses a challenge as it disrupts the continuity of the laminates, resulting in stress concentration and subsequent damage. To investigate the impact of various layup orientations and hole sizes on the tensile properties of open‐hole GLARE laminates, this study conducted axial tensile tests. Additionally, the tensile damage process was monitored using DIC and AE techniques, enabling the identification of damage patterns and the analysis of their evolution. The results demonstrate a noteworthy decline in the ultimate strength and failure strain as the size of the opening increases. Moreover, the retention rate of failure strain displays a marked sensitivity to the layup orientation. In conjunction with observations made through DIC and SEM, the k‐means++ algorithm successfully clustered peak frequencies, thereby revealing distinct damage patterns and their corresponding frequency ranges as aluminum alloy damage [0–90 kHz], matrix cracking [104–174 kHz], fiber/matrix debonding [175–224 kHz], interlaminar delamination [234–300 kHz], and fiber fracture [304–469 kHz]. AE cumulative counts were utilized to evaluate the progression of individual damage modes. The results emphasize that matrix cracking demonstrates the most substantial cumulative counts, whereas damage to the fibers and aluminum alloy noticeably affects the load‐carrying capability of the laminate. Furthermore, the fibers/matrix debonding and interlaminar delamination, exhibit heightened susceptibility to layup orientation and hole size. Highlights The tensile performance evaluation of GLARE laminates with open‐hole varying layup orientations and hole sizes was investigated. A combination of DIC and AE techniques was used to monitor the tensile damage process. Damage pattern was identified based on the observations of DIC and SEM. An approach based on Pearson's correlation coefficient and k‐means++ clustering algorithm was used for damage pattern recognition in GLARE laminates. AE cumulative counts were employed to assess the evolution of each damage mode.

Study on a numerical calculation method of fatigue behavior in Glare Panel

Modelling Fatigue Behaviours and Lifetimes of Novel GLARE Laminates under Random Loading Spectrum

Short beam shear damage analysis of GLARE laminates based on digital image correlation and finite element analysis

Dynamic impact behavior and notched fatigue life of GLARE laminates

Finite Element Analysis of the Fatigue Crack Tip Parameters in the Glass Fiber Reinforced Aluminum Alloy Laminates under Tension-Compression Loading

Failure Behavior of a Sandwich Beam with GLARE Face-Sheets and Aluminum Foam Core under Three-Point Bending

De Lamination And Fatigue Crack Growth Behavior In Fiber Metal Laminates (Glare) Under Single Overloads

Experimental study for the effect of hole notched in fracture mechanics of GLARE and GFRP composites subjected to quasi-static loading

Identifying the contributions of constituents to the fracture performance and failure mechanism of fiber metal laminate

Assessment of tensile damage mechanism of open‐hole GLARE laminates based on acoustic emission and digital image correlation techniques

Bending behavior and damage evolution of GLARE laminate using in‐situ AE technology and FEM

Three-Dimensional BEM and FEM Submodelling in a Cracked FML Full Scale Aeronautic Panel

Characterizing damage patterns and evolution in Multi-Hole GLARE laminates under tensile load via integrated AE and DIC techniques

Fatigue Tests of Single Layer and Laminated Glass Plates with Point Supports

Effect of Anodizing Process on Inter Laminar Shear Strength of GLARE Composite through T-Peel Test: Experimental and Numerical Approach

Quasi‐static fracture characterization of fiber metal laminate with crack resistance curve based on δ5

Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact

Delamination in GLARE laminates under low velocity impact

Energy dissipation mechanism of fiber metal laminate under low-velocity impact

Notched behavior of hybrid glass/aluminum/titanium fiber metal laminates

Delamination Behavior of an Advanced Al-Li Alloy Laminate During Fatigue Crack Growth