Abstract:The influence of chromium, manganese, carbon content and quenching modes on the formation of the structure, metastability of austenite and properties wear-resistant cast iron alloying system Fe-Cr-Mn-C with small additions of titanium, copper, silicon in various variations was investigated. The metallographic, durometric research methods, tests for dynamic bending, impact-abrasive wear resistance were applied. The regularities of changes in the phase composition and microstructure under the influence of the heating temperature for quenching in the range from 920 to 1070 °C with cooling in sand have been established. With an increase in the heating temperature for quenching in the structure of cast irons, the content of austenite increases and the content of quenching martensite decreases. The amount of carbide phases of compositions (Fe, Cr)3C, (Cr, Fe)7C3, (Cr, Fe)23C6 and titanium carbonitrides TiCN, depending on the content of carbon and alloying elements, as well as the heating temperature for quenching, varies within 20...35 %. A significant contribution of deformation induced phase transformations - martensitic, dynamic aging, occurring in the surface layers in the process of testing in the formation of impact-abrasive wear resistance of cast irons was revealed. It is characterized by the effects of deformation self-hardening, manifested in the increase in the hardness of the surface (working) layer within HRC = 2...9 and relaxation of microstresses. The formation of optimal martensitic-austenitic-carbide metastable structure could be provided at the optimal ratio of alloying elements and under the influence of heat treatment at which the effect of deformation self-hardening at wear that increases drastically the wear resistance of the investigated cast irons could be realized. The developed cast irons of optimal compositions have shown high economic efficiency in the production of working bodies of shot-blast machines, sand-throwers, protective lining plates of sintering-blast furnace equipment. They can be recommended for the manufacture of various high-wear machine parts of machines operating under conditions of impact-abrasive andabrasive wear.

Study on Microstructure and Friction of Bimetal 1.5cr4.8ni with Cast Iron and Low Carbon Steel

Effect of Hot-Rolling Deformation on Microstructure and Sliding Wear of High-Chromium Cast Iron

Fabrication of a Composite Material of High‐Chromium Cast Iron Dispersed in Low‐Carbon Steel by Hot‐Rolling Process

Experimental Investigation on the Mechanical and Tribological Coupled Behaviour of Bimetal Composite under Different States

Analysis of Heat Transport and Thickness of Bimetal Composition Layer Between Low-Alloy Steel and High-Chromium White Cast Iron

Study on Fragmentation and Dissolution Behavior of Carbide in a Hot-Rolled Hypereutectic High Chromium Cast Iron

Microstructures of carbon steel/high chromium iron composites prepared by centrifugal casting-hot rolling process

Investigations on Microstructures and Properties of B Containing Cast Steel for Wear Resistance Applications

Wear Behavior and Microstructure Changes of a High Chromium Cast Iron: The Combined Effect of Heat Treatment and Alloying Elements

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Microstructure and Mechanical Properties of High-Chromium Cast Iron/Low-Carbon Steel Composite Prepared by Hot Rolling Process

Characterization of Microstructure and Mechanical Properties of High Chromium Cast Irons Using Sem and Nanoindentation

Influence of Compositions and Heat Treatment on Metastability of Structure and Properties of Wear-Resistant Cast Irons of the Fe-Cr-Mn-C System

Processing and Wear Resistance of Carbon-Steel/High-Cr-Cast-Iron Bimetal Composite

Effect of Microstructures on the Tribological Performance of Medium Carbon Steel

Influence of Graphite Morphology and Chromium Content on Tribological Properties of Cast Iron under Dry Sliding

Sliding Wear of Cast-Iron Coatings and Cast-Iron-cast-iron Pairs in Lubricated Contact

MicrostructurMicrostructure and Properties and Fracture Surface Analysis of a Mediumcarbon and Medium Cr Wear-Resistant Steel

Effect of the Microhardness Difference Between Base Metal and Bionic Coupling Unit on Wear Resistance of Gray Cast Iron

Microstructure and Properties of Low and Medium Carbon of High-boron Cast Steel

Influence of Boron on Microstructure and Mechani cal Properties of Abrasive Wear Resistant Ductile Cast Iron