Influence of Graphite Morphology and Chromium Content on Tribological Properties of Cast Iron under Dry Sliding

Chen Yue,Shen Bailing,Zhang Yongzhen,Ni Feng,Xing Jiandong

DOI: https://doi.org/10.3321/j.issn:1001-0963.1999.02.011

1999-01-01

Journal of Iron and Steel Research International

Abstract:The influence of graphite morphology and chromium content on tribological properties of cast iron against asbestos base frictional material under dry sliding was studied by MM - 200 wear tester. The experimental results indicate that the cast iron with vermicular graphite morphology possesses the lowest wear loss rate. The friction coefficient of the grey cast iron is the highest, while that of the spheroidal graphite cast iron is the lowest. The addition of chromium to vermicular graphite cast iron made its wear resistance increase greatly and its frictional coefficient decrease slightly. Especially, under the condition of high sliding velocity and high contact pressure, the wear resistance of vermicular graphite cast iron with 1.5 % of chromium is 4 times higher than that of common vermicular graphite cast iron. With the increase of contact pressure, the wear rate increases and the frictional coefficient dicreases. The decrease of the frictional coefficient with the increase of contacting pressure is smaller at high sliding velocity than at low sliding velocity. The improvement on tribological properties due to addition of chromium to vermicular graphite cast iron is more obvious at high sliding velocity.