Abstract:Polyvinyl chloride (PVC)-based granulated adsorbents with high mechanical stability have proven effective for extracting lithium from salt lake brine on a commercial scale. However, granular materials with high adsorption selectivity for Na + /Li + separation and long service life still remain a great challenge. Here, we prepared granulated spherical adsorbents by a phase conversion method using PVC as a binder; PEG, PMMA, PAN, and PAA as hydrophilic co -binders; and Li 1.33 Mn 1.67 O 4 (LMO) as a powder adsorbent. Among these materials, P-PAA exhibited excellent hydrophilicity and excellent binder compatibility, facilitating the dispersion of LMO powders and ensuring high adsorption. Moreover, the mechanism of action of the PVC/PAA binders was first explored via experiments and simulations, which revealed that Li + migration was promoted and occurred primarily on LMO rather than on binders, so nonselective adsorption decreased. Therefore, P-PAA demonstrated exceptional Li + adsorption capacity (12.9 mg/g) and selectivity for Li + (distribution factor of 1391.3 mL/g) over other coexisting cations and a separation factor of alpha Li Na = 718, which are greater than those of other adsorbents reported in the literature. Furthermore, the unique structure of P-PAA, which was obtained by interconnecting larger core pores (5 - 10 mu m) and abundant smaller pores (0.5 - 1 mu m), accelerated the water/ion transfer kinetics without causing powder leakage. Hence, the lifespan of these materials has been extended, as salt crystals or internal cracks did not form during long-term cyclic use, unlike in the case of other granules. All of the above factors made P-PAA effectively recover Li + from Puguang gas brine, which contains a high sodium salt content and organic pollutants, with an efficiency of 98.4 %. All these properties demonstrate that P-PAA could be used in an appealing and competitive manner for industrial processes.

Lithium Adsorption of PVC-Li4Mn5O12 Ion-Sieve

Adsorption and Desorption Behavior of Lithium Ion in Spherical PVC–MnO2 Ion Sieve

Granulation to LiMn_2O_4 Ion-Sieve and Its Lithium Adsorption Property

Granulation to LIMn204 ion-sieve and its lithium adsorption property

Preparation and Adsorption Performance of Polyvinyl Chloride/Polyacrylonitrile Blended Lithium Ion-Sieve Membrane

Preparation and Characterization of PVDF/P（MMA-co-DMAEMA） Separators for Lithium Battery

Preparation of PVA/tetra-ZnO Composite with Framework-Supported Pore-Channel Structure and the Removal Research of Lead Ions

Lithium Selective Adsorption on 1-D MnO2 Nanostructure Ion-Sieve

Synthesis of H2TiO3-PVC lithium-ion sieves via an antisolvent method and its adsorption performance

Nanostructure Ion-Sieves for Lithium Adsorption

Synthesis of High Specific Surface Lithium-Ion Sieve Templated by Bacterial Cellulose for Selective Adsorption of Li+

Highly Selective Granulation Adsorbents for Lithium Recovery from Gas Field Brine: Selectivity, Kinetics and Mechanism

Lithium Ion Recovery from Brine Using Granulated Polyacrylamide–mno2 Ion-Sieve

Practical synthesis of manganese oxide MnO2·0.5H2O for an advanced and applicable lithium ion-sieve

Enhancement of Lithium Extraction from Low Grade Brines by High Hydrophilic Blend Membrane Using Mno 2 Ion Sieve As Adsorbents

Enhancement of lithium extraction from low grade brines by highly hydrophilic blend membranes using MnO 2 ion sieve as adsorbents

Synthesis of High Specific Surface Lithium ion Sieve Templated by Bacterial Cellulose for Selective Adsorption of Li+

MnO2 ion-sieve for lithium adsorption from aqueous resources

Preparation and Lithium Adsorption of Titania Ion-Sieves

An ion sieve-tailored biomimetic porous nanofibrous as an efficient adsorbent for lithium extraction from brine

Preparation of layered lithium ion-sieve by solid-phase method and their lithium extraction performance