E-Field Tuning Microwave Frequency Performance Of Co2fesi/Lead Zinc Niobate-Lead Titanate Magnetoelectric Coupling Composites
Shandong Li,Ming Liu,Jing Lou,Shawn Beguhn,Jianpeng Wu,Jie Qiu,Jianhua Lin,Zhiyi Cai,Yi Hu,Feng Xu,Jenqgong Duh,nian x sun
DOI: https://doi.org/10.1063/1.3670979
IF: 2.877
2012-01-01
Journal of Applied Physics
Abstract:Nanocrystalline Co2FeSi Heusler alloy films were deposited on single crystal lead zinc niobate-lead titanate substrates. It is revealed that this multiferroic composite exhibits very strong continuously electric field (E-field) tunable microwave frequency characteristics. With an increase of the E-field intensity from 0 to 6 kV/cm, the ferromagnetic resonance field H-r shifts by 348 Oe along the easy axis direction, being equivalent to 58 Oe cm/kV, and the ferromagnetic resonance frequency f(FMR) dramatically increases from 2.2 to 6.1 GHz with an increment of 3.9 GHz or an increment ratio of 177%; moreover, the damping constant alpha decreases from 0.0150 to 0.0085. These features demonstrate that this multiferroic structure is promising in the fabrication of E-field tunable microwave components. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3670979]