Soft magnetic and structural properties of (FeCo)–(AlSi) alloy thin films
Takuma Nakano,Bhuwan Nepal,Yoshitomo Tanaka,Shuang Wu,Kyotaro Abe,Gary Mankey,Tim Mewes,Claudia Mewes,Takao Suzuki
DOI: https://doi.org/10.1016/j.jmmm.2020.166852
IF: 3.097
2020-08-01
Journal of Magnetism and Magnetic Materials
Abstract:<p>The dependences of static and dynamic magnetic properties on both substrate deposition temperature (<em>T<sub>S</sub></em>) and film-thickness (<em>d</em>) for (FeCo)-(AlSi) alloy thin films are discussed in conjunction with structure. The samples of a multi layered type (FeCo)-(AlSi) alloy thin films were fabricated at Ts by DC sputter-deposition onto (100) MgO substrates by using two targets of Fe<sub>75</sub>Co<sub>25</sub> and Al<sub>50</sub>Si<sub>50</sub>. For the first time, the DO<sub>3</sub> phase in the quaternary alloy films are realized for <em>T<sub>S</sub></em> at around 400 ℃ with <em>d</em> larger than 25 nm. The order parameter (<em>S</em>) was estimated by taking into account crystal structure factor, absorption factor, multiplicity factor, temperature factor, and Lorentz polarization factor. It is found that S increases with <em>d</em>, becoming nearly 1 for <em>d</em> larger than 50nm. Observations by high resolution transmission electron microscopy support this result. The coercivity (<em>Hc</em>) and effective damping parameter (<em>α<sub>eff</sub></em>) decrease with increasing <em>d</em> and remain nearly constant, approximately 4 Oe and 5×10<sup>-3</sup>, respectively. The result that <em>H<sub>C</sub></em> decreases with increasing <em>S</em> suggests that (FeCo)-(AlSi) thin films with the DO<sub>3</sub> phase are an attractive candidate for future high frequency device applications.</p>
materials science, multidisciplinary,physics, condensed matter