Large E-field Tunability of Magnetic Anisotropy and Ferromagnetic Resonance Frequency of Co-Sputtered Fe50Co50-B Film
Shandong Li,Qian Xue,Honglei Du,Jie Xu,Qiang Li,Zhipeng Shi,Xiaoyang Gao,Ming Liu,Tianxiang Nan,Zhongqiang Hu,Nian X. Sun,Weiquan Shao
DOI: https://doi.org/10.1063/1.4906752
IF: 2.877
2015-01-01
Journal of Applied Physics
Abstract:Fe27.45Co30.19B42.36 (referred to as FeCoB) films with 100 nm in thickness were co-sputtered on (011)-cut lead zinc niobate-lead titanate (PZN-PT) single crystal substrate under RF powers of 80 W for Fe50Co50 target and 120 W for B target, respectively. The anisotropy field HK of the FeCoB/PZN-PT multiferroic composite is increased by more than 10 times, from 56 to 663 Oe under the E-field from 0 to 7 kV/cm due to the strong magnetoelectric coupling, corresponding to a large tunability of HK of 86.7 Oe cm/kV. At the same time, the self-bias ferromagnetic resonance frequency fFMR is dramatically shifted upwards by an electric field from 2.57 to 9.02 GHz with an increment of 6.45 GHz, corresponding to E-field tunablity of fFMR 921.4 MHz.cm/kV. These features demonstrate that FeCoB/PZN-PT multiferroic laminates prepared under an integrated circuits process are promising in fabrication of E-field tunable monolithic microwave integrated circuits (MMIC) devices and their components.