Crystallization behaviors of ZrCuNiAlTi4 bulk amorphous alloy during continuous heating
Dawei Xing,Yongjiang Huang,Jun Shen,Li Yang,Jianfei Sun
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.07.012
2007-01-01
Rare Metal Materials and Engineering
Abstract:The crystallization behaviors of Zr56.6Cu17.3Ni12.5Al9.6Ti4 (at %) bulk amorphous alloy during continuous heating are investigated mainly by differential scanning calorimeter (DSC). The results show that with increasing of heating rates, all the characteristic temperatures including glass transition temperature T-g, onset crystallization temperature T. and peak crystallization temperatures T-p1, and T-p2 shift to higher temperatures while the relationship between the characteristic temperatures and the heating rates obeys the first order exponential decay relation. The activation energies E-g, E-x, and E-p, corresponding to characteristic temperatures T-g, T-x, and T-p, respectively, were obtained from the Kissinger and Ozawa equations. The calculated activation energies show good agreement by the Kissinger or Ozawa equations due to the almost invariability of the crystallization volume fraction at the characteristic temperatures for different heating rates. The values of E-g, E-x, E-p1, and E-p2 fellow the sequence of E-g approximate to E-p1 approximate to E-p2 < E-x.