Abstract:With the development of high-pressure technology, pressure as a thermodynamic parameter is an important variable to control and influence the glass transition of metal melt. Therefore, in order to explore the influence of pressure on the glass transition of zirconium (Zr) melt under rapid solidification, the molecular dynamics simulation method has been adopted to obtain Zr metallic glass (MGs) by rapid solidification at the cooling rate of 1.0 × 1011 K/s under five different pressures. The results indicate that the glass transition temperature (T g) and the topologically close-packed (TCP) clusters have increased with the increasing pressure, resulting in the reduction of configurational entropy. The second peak of the pair distribution function (g(r)) gradually changes from the left lower than the right to the left higher than the right. A13[1/S444 10/S555 2/S666], Z12[12/S555], and Z14[12/S555 2/S666] clusters increase significantly with the increasing pressure, which is the reason for the second peak splitting of the g(r) curve. At 57.5 GPa (P5), Z12 and Z14 which account for 16.8% are concentrated in space and form large nanoclusters with a layered distribution. In the layered structure, Z12 and Z12 are connected by edge-sharing (ES), but Z12 and Z14 are connected by intercross-sharing (IS). It is confirmed that the second peak splitting of the g(r) curve is mainly caused by Z12, Z14, and both connecting. The distance from the peripheral atom to the central atom corresponds to R2/R1 = 1.56, R3/R1 = 2, and R4/R1 = 2.46 of the g(r) curve, and R1–4 represents different radial distances respectively. These results provide theoretical guidance for understanding the influence of pressure on the microstructure of MGs.

Pressure Effect On Crystallization Temperature In Zr70pd30 Metallic Glass

Evidence Of Polymorphous Amorphous-To-Quasicrystalline Phase Transformation In Zr66.7pd33.3 Metallic Glass

Crystallization In Zr41.2ti13.8cu12.5ni10be22.5 Bulk Metallic Glass Under Pressure

Glass transition, crystallization kinetics and pressure effect on crystallization of ZrNbCuNiBe bulk metallic glass

Pressure Effect on Crystallization of Zr41ti14cu12.5ni10be22.5 Bulk Metallic Glass Prepared by Shock-Wave Quenching

Pressure Effect on Crystallization of Metallic Glass Fe 72 P 11 C 6 Al 5 B 4 Ga 2 Alloy with Wide Supercooled Liquid Region

Pressure Effect on Crystallization Kinetics in Zr46.8Ti8.2Cu7.5Ni10Be27.5 Bulk Glass

Crystallization of Cu_60Ti_20Zr_20 Metallic Glass with and Without Pressure

Crystallization of Zr41Ti14Cu12.5Ni10Be22.5 Bulk Metallic Glass under High Pressure Examined by in Situ Synchrotron Radiation X-Ray Diffraction

Crystallization of Pd40Cu30Ni10P20 Bulk Metallic Glass with and Without Pressure

High-pressure annealing driven nanocrystal formation in Zr50Cu40Al10 metallic glass and strength increase

Crystallization of Pd 40 Cu 30 Ni 10 P 20 Bulk Glass under Pressure

Phase Transformations in Metallic Glasses

Effect of topologically close-packed clusters on the pair distribution function of amorphous Zr under different pressures

Origin of pressure-induced crystallization of Ce75Al25 metallic glass.

High-pressure Effects on Ti–Zr–Ni Metallic Glass and Its Corresponding Quasicrystal

Pressure Effect of Glass Transition Temperature in Zr46.8Ti8.2Cu7.5Ni10Be27.5 Bulk Metallic Glass

Crystallization of Bulk Zr 48 Nb 8 Cu 14 Ni 12 Be 18 Metallic Glass

Crystallization of Bulk Zr48Nb8Cu14Ni12Be18Metallic Glass

Pressure-Induced Amorphous-To-Amorphous Reversible Transformation in Pr75al25

Crystallization in Pd40ni40p20 Glass