Abstract:This study explores an efficient and feasible method for production of non-commercial Co-Cr-Mo powder feedstock for Laser Powder Bed Fusion (LPBF), employing mechanical alloying (MA) with following thermal treatment. Elemental Co, Cr, and Mo powders were subjected to MA to create a powder nanostructured composite. Initially, the mechanically alloyed powder had a mixed-phase state, with ε-phase as the main one (about 95 wt%) and impurities of Cr 2 O 3 . However, an additional 1.5-hour of isothermal annealing at 400 °C successfully reduced the Cr 2 O 3 impurities and caused oxygen content to decrease, indicating a reduction in residual oxygen in the powder. This annealing process activated diffusion and induced relaxation of residual stresses, evidenced by decreased lattice microstrains: 0.8% for the Co-phase, 0.2% for both the Cr-phase and Mo-phase. Powder subjected to the thermal treatment was then utilized in LPBF to create bulk Co-Cr-Mo samples. The formed samples showed a typical LPBF microstructure represented by uniaxial cells and dendrites, with the distance between these structures not exceeding 3 μm. The samples showed homogenous elemental distribution, mixed-phase composition, and oxygen concentration not exceeding 5 wt%. In terms of mechanical properties , the LPBF samples exhibited a microhardness value of 4300 ± 200 MPa, ductility of 0.85, and yield strength of 1.4·10 3 MPa. Our method yields results comparable to those obtained from commercially spherical powder, indicating that our cost-effective approach does not sacrifice product quality. It represents a substantial cost reduction, approximately 4.5 times lower than that of commercial spherical powder, thereby highlighting the economic efficiency of our powder feedstock preparation for LPBF. Our findings underscore the potential of mechanically alloyed and thermally treated powder in LPBF. This worthwhile and efficient method of preparation powder feedstock breaks ground for more comprehensive facilities in 3D printing, cut down on cost of production with maintaining the high-quality output.

Effect of Gas Atmosphere in Aluminobarothermal Synthesis on the Structure of Metal Matrix Composites Based on Fe – Cr – Mn – Mo Alloy

Effects of Ambient Gasses on the Magnetic Properties of Fe84.8Zr3.4Nb3.4B7.4Cu1 Nanocrystalline Alloy

Effect of Nitrogen Protective Atmosphere on Microstructure and High Temperature Erosion Property of TiAl3 and Cr3C2 Composite Coatings

Effects of Heat Treatment on Structure Transformation of Cr/Al Composite Coatings

Carbon Alloying of Metal Matrix Composites Based on Fe – Cr – Mn – Mo – N – C Alloys During Their Manufacturing by the Aluminobarothermic Variant of the SHS Method

Effect of nitrogen protective atmosphere on microstructure and property of nanocomposite coating

In-situ synthesis of nitrides and oxides through controlling reactive gas atmosphere during laser-powder bed fusion of Fe-12Cr-6Al

Influence of Carbon on the Wear Resistance, Strength, and Hardness of Composites with a Fe−Cr–Mn–Mo–N–C Matrix

Effect of N2- and CO2-Containing Shielding Gases on Composition Modification and Carbonitride Precipitation in Wire Arc Additive Manufactured Grade 91 Steel

Effect of AlN on the Mechanical and Electrochemical Properties of Aluminum Metal Matrix Composites

Microstructure and High-Temperature Mechanical Properties of CrMnFeCoNi/TiAl Composites Prepared by Powder Metallurgy

Revealing the Microstructure Evolution and Mechanical Properties of Al2O3-Reinforced FCC-CoCrFeMnNi Matrix Composites Fabricated via Gas Atomization and Spark Plasma Sintering

Effects of heat treating atmosphere on the phase composition and magnetic properties of Nd10Fe79Zr1Co4B6 alloy

Effects of Al 2 O 3 micro/nanoparticles on the microstructure and corrosion behavior of W–Ni–Fe matrix through spark plasma sintering process

Influence of Nitrogen Content on the Microstructure Evolution and Oxidation Resistance toward Ambient Air of CrAlSiN Coatings Deposited by FCVAD Technique

From Raw Elements to 3D Samples: An Economical Route for Co-Cr-Mo Alloy Fabrication

Microstructure and Mechanical Properties of the AlCrFeCoNip/AZ91D Composites After Heat Treatment

The effect of melt temperature on the mechanical properties of cast ASTM F75 CoCrMo alloy as explained by nitrogen and oxygen content

MECHANICAL ALLOYING WITH PARTIAL AMORPHIZATION OF FE–CR–CO–NI–MN MULTICOMPONENT POWDER MIXTURE AND ITS SPARK PLASMA SINTERING FOR COMPACT HIGH-ENTROPY MATERIAL PRODUCTION

Microstructure Evolution of FeNiCoCrAl1.3Mo0.5 High Entropy Alloy during Powder Preparation, Laser Powder Bed Fusion, and Microplasma Spraying

In-situ synthesis of Yttria-based precipitates and their effects on Fe12Cr6Al in laser powder bed fusion