Investigating the impact of gamma irradiation and temperature on vacancy formation and recombination in ZrB 2 ceramics using positron annihilation spectroscopy
Samir F. Samadov,Nguyen V.M. Trung,Alexander A. Donkov,Aleksey A. Sidorin,Oleg S. Orlov,Ertuğrul Demir,Oktay A. Samedov,Sakin H. Jabarov,Nguyen V. Tiep,Evgeni P. Popov,Matlab N. Mirzayev
DOI: https://doi.org/10.1016/j.jnucmat.2024.155242
IF: 3.555
2024-06-19
Journal of Nuclear Materials
Abstract:In the presented work, the mechanism of evolution of defects in the crystalline structure after irradiation with 1500 kGy and 3000 kGy absorption dose at room temperature in a 60 Co gamma source was studied, using 43 nm sized ZrB 2 crystals. The crystals were characterized by a purity of 99.9%, a powder density of 0.23 g/cm 3 , a specific surface area of 80 to 120 m 2 /g, and a hexagonal P6/m mm spatial structure. The dose rate applied was 6.05 Gy/s, with 1.17 and 1.37 MeV energy lines. The effect of particles resulting from the decay of Na 22 radioactive isotope β + with an activity of 10.5 μCi, as well as gamma quanta with an energy of 1.27 MeV, on the core and valence electrons and vacancies in the crystal structure was studied using Positron Annihilation Lifetime Spectroscopy (PALS) and Doppler broadening analysis methods. Additionally, the changes in the S and W parameters, which characterize the distribution of defects within the volume of the ZrB 2 crystal, were studied using the Doppler broadening method. For unannealed material, the positron lifetime τ 1 component varied between 174±2 ps and 181±1 ps. After annealing, the positron lifetime component τ 2 was decreased from 290±3 ps to 226±3 ps, and the intensity component I 2 increased from 17.49% to 40 % depending on the radiation dose. The calculated values of the positron lifetime τ for one boron vacancy from ABINIT and MIKA packages were found to be 172 ps and 145 ps, respectively. The material was observed to satisfy the necessary functional conditions at gamma doses not exceeding 3000 kGy.
materials science, multidisciplinary,nuclear science & technology