Abstract:In the present work, a novel and facile process has been proposed to fabricate porous Si2N2O-Si3N4 multiphase ceramics with low dielectric constant (εr＜4.0). Since silica poly-hollow microspheres could serve as the source of SiO2 and the pore-forming agent, they have been introduced into Si3N4 slurry through the gelcasting technique. This process is benefited from the liquid phase sintering reaction between SiO2 and Si3N4 with the aid of sintering additives, leading to in-situ synthesis of Si2N2O phase and porous structure. The content of silica poly-hollow microspheres has great influence on the properties of the final products. It indicates that Si2N2O phase would become the major phase when the content of silica poly-hollow microspheres was above 25wt%. Furthermore, the micromorphology results reveal that the content of pores with many smaller aggregate microspheres increases as microspheres amount rises. As a result, along with the addition of silica poly-hollow microspheres, the bulk density decreases to 1.32±0.01g/cm3, and open porosity ranges from 28.4±0.4% to 52.0±0.5%. Porous Si2N2O-Si3N4 multiphase ceramics prepared with 25wt% silica poly-hollow microspheres addition possess flexural strength of 42.3±3.8MPa, low dielectric constant of 3.31 and loss tangent of 1.93×10−3. It turns out to be an effective method to fabricate porous Si2N2O-Si3N4 composites with excellent mechanical and dielectric properties, which could be applied to radome materials.

High Performance Porous Wave-Transmitting Silicon Nitride Ceramics by Gel-Casting Technique

Fabrication and Properties of Porous Si3N4 Ceramic by Gel-Casting Technique

Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by a New Water-Based Freeze Casting

Mechanical and dielectric properties of porous Si3N4 ceramics prepared by modified water‐based gel casting

Preparation and Properties of Pressureless-Sintered Porous Si 3 N 4

Electromagnetic wave-transparent porous silicon nitride ceramic prepared by gel-casting combined with in-situ nitridation reaction

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Lightweight, High-Strength, and Broadband Transmission Porous Si3N4 Ceramics

Investigation of Gel Casting Preparation of Micro-Porous Si_3N_4 Ceramics

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Preparation, mechanical, dielectric and microwave absorption properties of hierarchical porous SiCnw-Si3N4 composite ceramics

High-strength and low-dielectric porous Si3N4 ceramics prepared by gelcasting using DMAA

Preparation and Properties of Micro porous Si3N4 Ceramics by Gelcasting

Fabrication and Properties of Porous Si3N4 Ceramic with High Porosity

Mechanical and dielectric properties of porous and wave-transparent Si3N4-Si3N4 composite ceramics fabricated by 3D printing combined with chemical vapor infiltration

Gelcasting Preparation of Porous Silicon Nitride Ceramics by Adjusting the Content of Monomers

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Dielectric Properties in GHz Range of Porous Si3N4–BN–SiO2 Ceramics with Considerable Flexural Strength Prepared by Low Temperature Sintering in Air

In-situ Reaction Synthesis of Porous Si2N2O-Si3N4 Multiphase Ceramics with Low Dielectric Constant Via Silica Poly-Hollow Microspheres