Abstract:This study investigates the cold formability of twin-roll cast and rolled magnesium strips, specifically focusing on AZ31 and ZAX210 alloys. The aim is to assess the suitability of these alloys for various forming processes. The mechanical properties and formability characteristics of the strips were thoroughly examined to provide insights into their potential applications in transportation industries such as automotive and aerospace. The AZ31 and ZAX210 alloys were subjected to twin-roll casting and rolling processes to produce thin strips. The resulting strips were then evaluated for their cold formability. The results indicate that both alloys exhibit favourable cold formability. The ZAX210 alloy, in particular, demonstrates medium strengths with an average tensile strength of approximately 240 MPa at room temperature. The 0.2% proof stress values range between 136 MPa and 159 MPa, depending on the sampling direction. The total elongation values vary from 28% in the transverse direction to 32% at a 45° angle, indicating excellent ductility. Comparing the two alloys, the AZ31 alloy shows higher strengths due to its higher aluminium content. However, it also exhibits a more pronounced directional dependence of mechanical properties due to the formation of a strong basal texture during hot rolling. The transverse direction experiences reduced total elongation compared to the rolling direction, achieving only about 50% of the total elongation. The average Erichsen Index recorded for AZ31 and ZAX210 strips were 4.9 mm and 7.1 mm, respectively. The ZAX210 strip displays superior formability, which can be attributed to the fine-grained microstructure and the texture softening resulting from the weakening of the basal texture intensity and the splitting of the basal pole towards the rolling direction. In conclusion, the investigated twin-roll cast, rolled and annealed AZ31 and ZAX210 magnesium strips exhibit promising cold formability characteristics. The findings of this study contribute to the understanding of their mechanical behaviour and can guide the selection and optimisation of these alloys for various forming applications.

Tensile Properties Of Three Preform-Annealed Magnesium Alloy Sheets

Comparison of tensile properties and crystallographic textures of three magnesium alloy sheets

Formability and Process Conditions of Magnesium Alloy Sheets

A new magnesium sheet alloy with high tensile properties and room-temperature formability

Mechanical Behavior Characterization of Magnesium Alloy Sheets at Warm Temperature

Improved Ductility of Magnesium Alloy Sheets by Pre-Hardening and Annealing

Cold Formability of Twin-Roll Cast, Rolled and Annealed Mg Strips

Fabrication of Excellent Mechanical Properties AZ31 Magnesium Alloy Sheets by Conventional Rolling and Subsequent Annealing

Effect of Pre-stretch Strain at High Temperatures on the Formability of AZ31 Magnesium Alloy Sheets

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Strain Rate and Temperature Effects on Formability and Microstructure of AZ31B Magnesium Alloy Sheet

Forming Limits of Magnesium Alloy AZ31B Sheet at Elevated Temperatures

Influence of Microstructure and Texture on Formability of AZ31B Magnesium Alloy Sheets

Enhanced Stretch Formability and Mechanical Properties of a Magnesium Alloy Processed by Cold Forging and Subsequent Annealing

Enhancement of Mechanical Properties and Corrosion Resistance of Magnesium Alloy Sheet by Pre-Straining and Annealing

Formability of Az31 Magnesium Alloy Sheets at Warm Working Conditions

Mechanical Behavior of AZ31B Magnesium Alloy Sheet at Different Strain Rates and Stress States

Microstructures and tensile properties of commercial AZ31B magnesium alloy sheets

Improved formability of Mg-3Al-1Zn alloy by pre-stretching and annealing

Effect of pre-strain levels and high temperature annealing on the formability of AZ31 Mg alloy thin sheet during stretch deformation

Enhanced Mechanical Properties of AZ31B Magnesium Alloy Thin Sheets Processed by On-Line Heating Rolling