Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Comparison of tensile properties and crystallographic textures of three magnesium alloy sheets

Microstructure, Texture Evolution, and Mechanical Properties of Thin AZ31B Mg Alloy Sheets Prepared by Two-Stage Rolling

Texture and Its Effect on Mechanical Properties of AZ31 Magnesium Alloy

Texture Evolution of AZ31 Magnesium Alloy Sheets During Warm Rolling

Effect of texture types on microstructure evolution and mechanical properties of AZ31 magnesium alloy undergoing uniaxial tension deformation at room temperature

Effect of rolling reduction on microstructure, texture, mechanical properties and mechanical anisotropy of AZ31 magnesium alloys

Excellent Room-Temperature Ductility and Formability of Rolled Mg–Gd–Zn Alloy Sheets

Mechanical properties and texture evolution during hot rolling of AZ31 magnesium alloy

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Microstructure and Mechanical Properties of Mg–3Al–Zn Magnesium Alloy Sheet by Hot Shear Spinning

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Microstructure and Texture Evolution of the Magnesium Alloy ZMX210 during Rolling and Annealing

Research on 200 ℃ Tensile Properties of Rolled Mg-8Al-4Sr-1Y Magnesium Alloy Sheet

Microstructure and Tensile Properties of Mg-3Al-1Zn Sheets Produced by Hot-Roller-cold-material Rolling

Influence of cryogenic treatment time on the mechanical properties of AZ31 magnesium alloy sheets after cross-rolling

Room-temperature Ductility and Anisotropy of Two Rolled Mg–Zn–Gd Alloys

Mechanical Properties and Texture Evolution During Rolling Process of an AZ31 Mg Alloy

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Mechanical Properties and Constitutive Analysis of Extruded AZ31B Magnesium Alloy

Microstructure evolution and mechanical property of Mg-3Al alloys with addition of Ca and Gd during rolling and annealing process

Property Improvements in Fine–grained Mg–Zn–Zr Alloy Sheets Produced by Temperature–step–down Multi–pass Rolling