Abstract:In this study, a novel technique of consecutive multi-pass cooperative lowered-temperature rolling (CMCLR) was proposed for the first time, with the purpose of preparing high performance wrought magnesium alloys. Based on this, a highly ductile magnesium alloy sheet could be effectively produced from ingot. The corresponding microstructure could directly evolve from coarse dendrites to equiaxed grains with an average size of similar to 5 mu m, which was attributed to the intense dynamic recrystallization (DRX) during isothermal deformation. The equivalent strain gradually decreased from the surface to the interior and edge of the rolled sheet due to the anisotropic plastic deformation. Instead, the temperature of the core of the sheet was slightly higher than that of the surface due to the deformation heat effect. The basal texture in the RD-TD plane generally weakened in the form of the splitting of basal texture toward the RD and the broadening of basal plane away from the pole center due to texture randomization dominated by DRXed grains. The exceptional ductility of more than 28.7% together with acceptable ultimate tensile strength of not less than 267 MPa was ascribed to the progressive work hardening as a result of seamless switching of multiple deformation modes, i.e., basal dislocation-slip-mediated deformation was preferentially operated and then was substituted by twinning-controlled deformation and non-basal dislocation-slip-dominated deformation. The selection of {10 (1) over bar2} twin variants agreed well with geometrical compatibility factor (m') criterion instead of Schmid's law. The activated twin variants nearly engulfed the whole parent grains for the sake of preserving compatible deformation continuity at ambient temperature, giving rise to the formation of TD-split texture. Comparatively, the {10 (1) over bar2} twinning could randomize the basal texture via reorienting grain orientations which in turn facilitated the reactivation of dislocation slip systems in the case of high temperature deformation.

Room-temperature Ductility and Anisotropy of Two Rolled Mg–Zn–Gd Alloys

Excellent Room-Temperature Ductility and Formability of Rolled Mg–Gd–Zn Alloy Sheets

Influence of Texture and Grain Size on the Room-Temperature Ductility and Tensile Behavior in a Mg–Gd–Zn Alloy Processed by Rolling and Forging

Influences of Tensile Temperature on the Mechanical Properties of Rolled Mg-Zn-Gd Sheets with Non-Basal Texture

Effects of Gd Concentration on Microstructure, Texture and Tensile Properties of Mg–Zn–Gd Alloys Subjected to Large Strain Hot Rolling

Consideration of Castability and Formability for New Magnesium Alloys

Room-Temperature Strengthening, Portevin-Le Chatelier Effect, High-Temperature Tensile Deformation Behavior, and Constitutive Modeling in a Lightweight Mg-Gd-Al-Zn Alloy

Superplasticity and microstructure in Mg–Gd–Y–Zr rolled sheet

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of Rolling Parameters on Room-Temperature Stretch Formability of Mg–2Zn–0.5Ca Alloy

A Comparative Study of Texture and Ductility of Mg–1.2Zn–0.8Gd Alloy Fabricated by Rolling and Equal Channel Angular Extrusion

Microstructure and Mechanical Properties of Rolled Mg-12gd-3y-0.4zr Alloy Sheets

An Exceptional Ductility of AZ31 Magnesium Alloy Sheet Achieved by Consecutive Multi-Pass Cooperative Lowered-Temperature Rolling

Microstructure and mechanical properties of hot-rolled Mg–Zn–Nd–Zr alloys

Rolling Temperature and Subsequent Annealing on Microstructure, Texture and Mechanical Properties of Consecutive Rolled Mg-2.0zn-0.8gd Alloy

Activation of {1 01¯2} Twinning and Slip in High Ductile Mg–2.0Zn–0.8Gd Rolled Sheet with Non-Basal Texture During Tensile Deformation at Room Temperature

Origins of High Ductility Exhibited by an Extruded Magnesium Alloy Mg-1.8Zn-0.2Ca: Experiments and Crystal Plasticity Modeling

Microstructure, Mechanical Properties and Texture Evolution of Mg–Al–Zn–La–Gd–Y Magnesium Alloy by Hot Extrusion and Multi-Pass Rolling

Microstructure and Mechanical Properties of Rolled Sheets of Mg–Gd–Y–Zn–Zr Alloy: As-cast Versus As-Homogenized

Improving the Ductility of Mg-2.5Nd-0.5Zn-0.5Zr Alloy by Multi-Pass Hot Rolling