Abstract:Highlights • The high rolling temperature would impede the DRX occurrence for these final-rolled sheets. • The reduction of the volume fraction of this β phases led to the highest peak-aging hardness in R-450 °C sheet. • The precipitate chains in R-385 °C + A sheets were beneficial for strength and elongation. • The traditional precipitation characteristic in R-450 °C + A sheet was bad for elongation but good for strength. • The peak-aging R-450 °C sheet showed the highest strength, i.e. UTS of 518±17 MPa and YS of 438±18 MPa. In this investigation, a high-strength Mg-12Gd-1.0Er-0.5Zr (wt.%) alloy sheet was produced by hot extrusion (HE) and subsequent hard-plate rolling (HPR) at different temperatures. The results indicate that the microstructures of these final-rolled sheets are inhomogeneous, mainly including coarse deformed grains and dynamic recrystallized (DRXed) grains, and the volume fraction of these coarse deformed grains increases as the rolling temperature increases. Thus, more DRXed grains can be found in R-385 °C sheet, resulting in a smaller average grain size and weaker basal texture, while the biggest grains and the highest strong basal texture are present in R-450 °C sheet. Amounts of dynamic precipitation of β phases which are mainly determined by the rolling temperature are present in these sheets, and its precipitation can consume the content of Gd solutes in the matrix. As a result, the lowest number density of β phase in R-450 °C sheet is beneficial to modify the age hardening response. Thus, the R-450 °C sheet displays the best age hardening response because of a severe traditional precipitation of β' (more) and β Η / β Μ (less) precipitates, resulting in a sharp improvement in strength, i.e. ultimate tensile strength (UTS) of ∼ 518 ± 17 MPa and yield strength (YS) of ∼ 438±18 MPa. However, the elongation (EL) of this sheet reduces greatly, and its value is ∼ 2.7 ± 0.3%. By contrasting, the EL of the peak-aging R-385 °C sheet keeps better, changing from ∼ 4.9 ± 1.2% to ∼ 4.8 ± 1.4% due to a novel dislocation-induced chain-like precipitate which is helpful to keep good balance between strength and ductility.

Enhanced Mechanical Properties of AZ31B Magnesium Alloy Thin Sheets Processed by On-Line Heating Rolling

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Microstructure, Texture Evolution, and Mechanical Properties of Thin AZ31B Mg Alloy Sheets Prepared by Two-Stage Rolling

Grain refining and improving mechanical properties of AZ31 Mg alloy sheets by multi-pass warm rolling with falling temperature

Microstructure Evolution and Mechanical Properties of AZ31 Magnesium Alloy Sheets Prepared by Low-Speed Extrusion with Different Temperature

Microstructure and properties of AZ31 alloy by static recrystallisation at lower temperature

Ameliorating the edge cracking behavior of Mg-Mn-Al alloy sheets prepared by multi-pass online heating rolling

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Varying strain rates and elevated temperatures effects on the mechanical properties of AZ31B magnesium alloy

Strain Rate and Temperature Effects on Formability and Microstructure of AZ31B Magnesium Alloy Sheet

Influence of cryogenic treatment time on the mechanical properties of AZ31 magnesium alloy sheets after cross-rolling

Effects of Rolling-Cryogenic Process on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets

Effects of deformation temperatures on microstructures, aging behaviors and mechanical properties of Mg-Gd-Er-Zr alloys fabricated by hard-plate rolling

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Effect of Final Rolling Speed on Microstructure and Performance of AZ31 Magnesium Alloy Sheet under Small Strain Condition

Effects of Annealing Treatment on Mechanical and Damping Properties of ZK60 Magnesium Alloy Sheets

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Effects of cryogenic treatment on microstructure and mechanical properties of AZ31 magnesium alloy rolled at different paths

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

INFLUENCE OF ROLLING TEMPERATURE ON THE {1011}-{1012} TWINNING IN ROLLED AZ31 MAGNESIUM ALLOY SHEETS

Effect of Final Rolling Temperature on Microstructures and Mechanical Properties of AZ31 Alloy Sheets Prepared by Equal Channel Angular Rolling and Continuous Bending