Effects Of Heat Treatment On The Corrosion Resistance Of The Ni-Based G3 Alloy

Tian Wei,Xie Faqin,Zhao Xuehui
DOI: https://doi.org/10.3969/j.issn.1002-185X.2012.03.021
2012-01-01
Rare Metal Materials and Engineering
Abstract:The effect of the solution and aging treatment on the microstructure and precipitated phase of the G3 steel was investigated by TEM and SEM. And then, the effect of the microstructure change and precipitated phase on the corrosion resistance of G3 steel was analyzed by the corrosion test in high temperature and high pressure environment containing H2S/CO2. The results indicate that the solution treatment temperature should not exceed 1150 degrees C in order to avoid the much bigger grains. The carbide M23C6 precipitated in grain boundaries is increased, and the plate-like carbide M6C is formed inside grains with the aging temperature increasing. The formation of precipitated phase of chrome carbide leads to the severe pitting corrosion of the Ni-based alloy because a poor chromium area has been formed in intergranular sites so that the corrosion resistance of G3 alloys is reduced.
What problem does this paper attempt to address?