Abstract:Calcium hexaluminate (CA6) was synthesized using industrial γ-Al2O3 and CaO (w(CaO)≥99.0%) as starting materials. The starting materials were weighed according to n(CaO): n(γ-Al2O3) of 0.66, 0.86, 1.06, 1.26, and 1.46, respectively, ball milled, dried, and then dry pressed into specimens with the size of 6 mm×6 mm×40 mm. The specimens were fired at 1 550 °C for 3 h. Phase composition and microstructure of fired specimens were analyzed by XRD and SEM; volume shrinkage, apparent porosity, bulk density, and cold modulus of rupture were determined. The results show that: (1) the main phase of all the specimens with different molar ratios of CaO and γ-Al2O3 is CA6. A little α-Al2O3 is observed when the formulation is alumina-rich, and a small amount of CA2 is detected when the formulation is calcia-rich; (2) CA6 of all specimens is lamellar. For the formulation with rich alumina, the lamellar CA6 is obvious with clear profile. For the formulation with rich calcia, CA2 doesn't convert into CA6 completely because of short alumina; (3) when the molar ratio of CaO to γ-Al2O3 is 0.66, the specimen has the highest volume shrinkage. When it is 1.46, the specimen has the lowest apparent porosity and the highest bulk density. When it is 0.86, the specimen has the highest cold crushing strength of 30.9 MPa.

Sintering Procedure of Calcium Hexaluminate Ceramics

Novel Synthesis Method and Characterization of Porous Calcium Hexa‐Aluminate Ceramics

Preparation of Calcium Hexaluminate Using Al2o3 and White Beach Sand from Western Australia

Synthesis and Characterization of Calcium Aluminate Compounds from Gehlenite by High-Temperature Solid-State Reaction

Fabrication and Properties of CaAl12O19-Al2O3 Composite Ceramics

Effect of La2O3 on Structure and Properties of Calcium-Hexaluminate Prepared by Reaction Sintering

Preparation of Calcium Hexaluminate Using Al<sub>2</sub>O<sub>3 </sub>and White Beach Sand from Western Australia <sub> </sub>

Influence of molar ratio of CaO and γ-Al2O3 on synthesis of lamellar calcium hexaluminate

Influence of Holding Time on Preparation and Properties of Lightweight High Temperature Calcium Hexaluninate

In-situ synthesis of porous calcium hexa-aluminate ceramics and growth mechanism of the plate-like grains

Influence of molar ratio of CaO and γ-Al_2O_3 on synthesis of lamellar calcium hexaluminate

Preparation of High-Quality Porous Calcium Hexa-Aluminate Ceramics Using Salt As Both Reaction Medium and Pore-Former

A novel strategy for low-temperature fabrication of porous CA 6 ceramics using reactive CaCl 2 -KCl medium and its influence mechanism

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

FABRICATION AND PROPERTIES OF CALCIUM-HEXALUMINATE/MAGNESIUM-ALUMINIUM SPINEL COMPOSITES

Preparation and characterization of calcium hexaaluminate (CA6) porous ceramic for application in high-temperature flue gas filtration

Preparation of calcium hexaluminate porous ceramics by gel-casting method with polymethyl methacrylate as pore-forming agent

Kinetics and Mechanism of A Sintering Process for Macroporous Alumina Ceramics by Extrusion

Mineral Phase Transformation During the Sintering of the GreenBody of Electric Ceramics Made of Liuyang Clays

Thermal-assisted cold sintering study of Al2O3 ceramics: Enabled with a soluble -Al2O3 intermediate phase

Study on Synthesis of CA6 and MgAl2O4 with Dolomite As a Source of Calcium and Magnesium