Abstract:A high sintering temperature is required to acquire excellent performance in the production of porcelain but results in high fuel consumption. To prepare the porcelain with outstanding performance at a lower temperature, a self-produced additive containing calcium (CaK) was added into a three-component system of kaolinite–feldspar–quartz. XRD and SEM were used to characterize the samples. The toughening mechanism and Gibbs free energy were investigated. After introducing the CaK, the bending strength of the porcelain fired at 1513 K increased from 56.32 ± 0.65 MPa to 95.31 ± 0.63 MPa, which was 21.83% higher than that of the porcelain without CaK at an optimal firing temperature of 1603 K. The main crystal phase of the sample comprised mullite and quartz in the raw materials at 1453~1603 K. The anorthite was observed at 1453 K and interlocked with needle-shaped mullite at 1513 K in the porcelain after adding CaK, which resulted in the higher bending strength. Quantitative analysis indicated that the amount of anorthite decreased at 1513 K and disappeared at 1543 K; the amount of mullite increased with temperature. The Gibbs free energy of the reaction (CaO•Al2O3•2SiO2 + 2(Al2O3•2SiO2) → 3Al2O3•2SiO2 + CaO + 4SiO2) at high temperature was negative, which suggested that the formation of mullite (3Al2O3•2SiO2) from anorthite (CaO•Al2O3•2SiO2) was possible. These findings implied that the addition of CaK contributed to the appropriate phase composition and microstructure, and the excellent performance of the porcelain at a lower temperature. In addition, the transformation between anorthite and mullite was possible in the special raw material system. The results are of interest in producing anorthite/mullite ceramics at reduced sintering temperatures and the conversion between anorthite and mullite.

Mineral Phase Transformation During the Sintering of the GreenBody of Electric Ceramics Made of Liuyang Clays

Impact of the Mineral Composition and Sintering Temperature on the Synthesis of Anorthite Ceramics

The Effects of Mineral Composition and Sintering Temperature on Synthetic Mullite

Synthesis, Characterization and Sintering Behaviour of Indialite Ceramic from Fly Ash.

Phase-Field Simulation of Process in Sintering Ceramics

Preparation of Anorthite/Mullite In Situ and Phase Transformation in Porcelain

Study on Phase Behavior and Mechanical Properties of High Temperature Resistant Materials Prepared from Waste Electric Porcelain

The crystallization and microstructure evolution of lithium disilicate-based glass-ceramic

Effect of Mineral Composition and Sintering Temperature on the Synthetic Cordierite

Effects of Sintering Temperature on Phase and Physical Properties of Hejin Red Mud

Qantitative Pattern of the Change in Microstructure and Surface Properties of Electric Ceramic During Sintering Processes

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite

Electrochemical grand potential-based phase-field simulation of electric field-assisted sintering

Effect of Ce4+-modified amorphous SiO2 on phase transformation towards α-cordierite

Properties and Sintering Behavior of Ceramics Used Fly Ash and Red Mud As Raw Materials

Structural transformation and dehydroxylation of clay minerals in lithium-bearing clay

Study of phase transformation of calcium silicate using desert sand as raw materials

Experimental Study of High Temperature Phase Transformation for Pyrophyllite

PHASE TRANSFORMATION FOR CALCINED COAL MEASURES KAOLINITE

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals

Crystalline phase formation, microstructure and mechanical properties of a lithium disilicate glass–ceramic